The invention discloses an antistatic HDPE graft copolymer, which comprises the following components: 100 parts of HDPE, 4.5 to 5 parts of DM, 0.3 to 0.5 parts of DCP, 1.5 to 1.8 parts of stannous chloride, 1024 0.2 to 0.28 parts of antioxidant and 0.8 to 1.0 parts of polyethylene ester. In the extrusion process of HDPE, a functional antistatic agent, dimethylaminoethyl methacrylate (DM), is added to graft DM onto the macromolecular chain of HDPE under the action of DCP and catalyst. The grafted HDPE copolymer not only maintains its original comprehensive properties, but also greatly improves its antistatic ability, with surface resistivity of 1.8 *102_and volume resistivity. 3.8 x 106_. m, which enlarges its application range.
【技术实现步骤摘要】
一种抗静电HDPE接枝共聚物及其制备方法
本专利技术涉及聚合物接枝改性领域，具体涉及一种抗静电HDPE接枝共聚物及其制备方法。
技术介绍
高密度聚乙烯(HDPE)是综合性能优良的聚合物，原料来源丰富，成本低，被广泛应用于煤矿、石油、化工等行业。由于HDPE的电绝缘性好，在运输和使用过程中，容易产生积累静电，而静电放电时可引起火灾或爆炸事故。因此必须对HDPE做抗静电的处理，工业上对HDPE抗静电改性的方法有两种，一种是采用电镀、涂覆、粘贴等方法对HDPE制品表面进行处理，使其表面形成导电层，这种方法虽然有效但是成本高，产生的污染也较大，且难以处理形状复杂的制品；另一种方法是添加法，即在HDPE中添加抗静电剂或导电性填料(如导电炭黑、石墨、金属粉等)使得HDPE的抗静电性或导电性能得到提高，但是该方法由于抗静电剂的加入，HDPE制品的冲击强度和拉伸断裂应变值明显下降。故这两种对HDPE抗静电的处理方法都存在缺点，从而仍然限制HDPE的使用范围。
技术实现思路
本专利技术要解决的技术问题是克服现有技术中HDPE抗静电能处理时加入抗静电剂后HDPE制品的冲击强度和拉伸断裂应...
【技术保护点】
1.一种抗静电HDPE接枝共聚物，其特征在于，包括以下重量份数的各组分：HDPE 100份DM 4.5～5份DCP 0.3～0.5份氯化亚锡 1.5～1.8份抗氧化剂1024 0.2～0.28份聚乙烯酯 0.8～1.0份。
【技术特征摘要】
1.一种抗静电HDPE接枝共聚物，其特征在于，包括以下重量份数的各组分：HDPE100份DM4.5～5份DCP0.3～0.5份氯化亚锡1.5～1.8份抗氧化剂10240.2～0.28份聚乙烯酯0.8～1.0份。2.如权利要求1所述的抗静电HDPE接枝共聚物，其特征在于，包括以下重量份数的各组分：HDPE100份DM4.8份DCP0.4份氯化亚锡1.6份抗氧化剂10240.25份聚乙烯脂0.9份。3.如权利要求1所述的抗静电HDPE接枝共聚物的制备方法，其特征在于，包括以下步骤：(1)、在双螺杆挤出机的料斗1中加入HDPE；(2)、将DM、DC...
【专利技术属性】
技术研发人员：储文明，
申请(专利权)人：江苏益帆高分子材料有限公司，
类型：发明
国别省市：江苏,32