The invention provides a water-retaining admixture, whose main components include water reducing agent, retarder, air entraining agent, defoamer, viscosity thixotropic agent and water retaining agent, and the remaining amount is water. The invention also provides the preparation method and application of the water retaining admixture. The water-retaining admixture provided by the invention can not only ensure better cohesion of concrete, but also improve water-retaining performance of concrete, meet the working performance of various kinds of concrete, significantly improve concrete strength, increase concrete compactness and make concrete durable under poor raw materials such as discontinuous graded machine-made sand. In addition, the water-retaining admixture provided by the invention is used. The agent improves the pumping performance of concrete, reduces the phenomenon of pump blocking, and further saves human and material resources.
【技术实现步骤摘要】
一种保水型外加剂及其制备方法和应用
本专利技术属于混凝土外加剂
，具体涉及一种保水型外加剂及其制备方法和应用。
技术介绍
砂作为混凝土细骨料，是高性能混凝土中用量较大的原材料。由于天然砂石资源短缺，很多地方无砂可采，采用机制砂石取代天然砂石来配制高性能混凝土的趋势愈专利技术显，然而，由于大部分机制砂细度模数大、级配不连续、含泥量高，容易导致混凝土拌合用水量大，保水性差，粘聚性不够，最终使混凝土强度下降。当混凝土原材料质量不稳定时，要保证混凝土有较好的工作性能、力学性能与耐久性能，添加保水型外加剂就显得尤其重要。CN105585673A公开了一种混凝土增粘保水剂，该增粘保水剂以甲基烯丁基聚氧乙烯聚氧丙烯、不饱和一元羧酸或/和其衍生物、不饱和烯基磺酸或/和其钠盐份以及不饱和烯基有机硅交联剂为原料，经聚合得到，该专利技术还提供了制备上述混凝土增粘保水剂的方法，该专利技术提供的增粘保水剂应用于C30及以下级别混凝土时，增粘保水效果优异，混凝土流动性损失小，然而，该专利技术提供的增粘保水剂制备过程较繁琐且需加温，增加了制造成本。CN101538351B公开了一种聚羧酸...
【技术保护点】
1.一种保水型外加剂，其特征在于，包含以下质量百分比计的组分：减水剂15～35％，缓凝剂10～20％，引气剂0.1～0.5％，保水剂0.05～2％，碳酸钠0.5～1％，余量为水，所述减水剂为聚羧酸高性能减水剂。
【技术特征摘要】
1.一种保水型外加剂，其特征在于，包含以下质量百分比计的组分：减水剂15～35％，缓凝剂10～20％，引气剂0.1～0.5％，保水剂0.05～2％，碳酸钠0.5～1％，余量为水，所述减水剂为聚羧酸高性能减水剂。2.根据权利要求1所述的保水型外加剂，其特征在于，还包含消泡剂和粘度触变剂，所述消泡剂和粘度触变剂的质量百分比分别为0.5％和2％。3.根据权利要求2所述的保水型外加剂，其特征在于，所述的消泡剂为聚醚类合成消泡剂。4.根据权利要求2所述的保水型外加剂，其特征在于，所述的粘度触变剂为聚氨酯。5.根据权利要求1所述的保水型外加剂，其特征在于，所述的聚羧酸高性能减水剂的固含≥20％。6.根据权利要求1所述的保水型外加剂，其特征在于，所述...
【专利技术属性】
技术研发人员：张斌，罗伶平，
申请(专利权)人：长沙瑞联材料科技有限公司，
类型：发明
国别省市：湖南,43
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。