The invention relates to the field of titanium extraction from blast furnace slag, in particular to a method for judging the end point of carbonization smelting of blast furnace slag. The technical problem to be solved by the present invention is to provide a method for judging the end point of the carbonization smelting of blast furnace slag, including the following steps: when the following three conditions are met at the same time, the end point of the smelting can be judged: first, when the slag in the furnace rises and falls behind, when the slag liquid level is stable, the slag temperature is 1600 (+20 C); second, when the voltage is constant, the current is in the range of maximum (+5%). Hold for 10 minutes or more; Third, power consumption per ton of slag is more than 850 kWh. The method of the invention can accurately judge the end point of smelting and improve the carbonization rate of smelting.
【技术实现步骤摘要】
判断高炉渣碳化冶炼终点的方法
本专利技术涉及高炉渣提钛领域，特别涉及一种准确判断高炉渣碳化冶炼终点的方法。
技术介绍
攀西地区的钒钛磁铁矿占中国钛资源总量的90％以上，其中50％左右的钛经高炉炼铁后进入高炉渣中，成为TiO2含量为21～25％的高钛型高炉渣。目前来看，“高炉渣高温碳化—低温氯化”是高炉渣提钛领域最具产业化前景的路线，可有望规模化实现渣中钛资源的高附加值利用。高温碳化是高炉渣提钛技术的一项重要工艺，碳化率的高低直接影响提钛效率及产品质量，是该项工艺的一个重要控制指标。由于碳化渣中碳化钛含量的分析流程复杂，分析时间长，通常无法利用在线分析碳化渣成分来准确判断终点。以致出现出炉时机判断不准确，碳化率忽高忽低，产品指标波动大的情况，不但影响后续氯化工艺操作的稳定性，降低钛收率，还使整个高炉渣提钛工艺的技术经济性大大折扣。
技术实现思路
本专利技术针对高炉渣碳化冶炼过程中碳化钛分析周期长，无法立即用于现场生产指导的问题，本专利技术提供了一种准确判断高炉渣碳化冶炼终点的方法。该方法包括以下步骤：当同时满足以下三个条件时，则判断到达冶炼终点，第一：炉内熔渣经过上涨回...
【技术保护点】
1.判断高炉渣碳化冶炼终点的方法，其特征在于：包括以下步骤：当同时满足以下三个条件时，则判断到达冶炼终点，第一：炉内熔渣经过上涨回落后，炉渣液面稳定时，炉渣温度为1600±20℃；第二：恒定电压时，电流在极大值±5％范围内维持10min或以上；第三：吨渣电耗≥850kWh。
【技术特征摘要】
1.判断高炉渣碳化冶炼终点的方法，其特征在于：包括以下步骤：当同时满足以下三个条件时，则判断到达冶炼终点，第一：炉内熔渣经过上涨回落后，...
【专利技术属性】
技术研发人员：黄家旭，张溅波，王东生，赵青娥，
申请(专利权)人：攀钢集团攀枝花钢铁研究院有限公司，
类型：发明
国别省市：四川,51