The invention discloses a method for surface treatment of metal products. The metal products are washed with clean water, wetted with potassium permanganate solution and dilute hydrochloric acid respectively, and finally coated with a layer of wear-resisting agent on the surface, and coated with vacuum coating method to obtain the finished metal products. Compared with the traditional technology, the sub-metallic ions on the surface of metal products are oxidized by adding potassium permanganate, and then cleaned by adding acid solution after forming chloride salt on the surface of metal products. Finally, the surface service life of metal products is guaranteed by combining wear-resistant agent with metal products.
【技术实现步骤摘要】
一种金属制品表面处理方法
本专利技术属于金属制造领域，具体涉及一种金属制品表面处理方法。
技术介绍
金属及其制品在加工过程中常会在表面沾染各种污物和杂质，而且，由于可能长期在户外使用，因此金属制品必须具备很好的稳定性及耐磨性，金属制品表面必须经过一定的处理后才能更好地使用。
技术实现思路
专利技术目的：本专利技术的目的在于针对现有技术的不足，提供一种金属制品表面处理方法。技术方案：为了达到上述专利技术目的，本专利技术具体是这样来实现的：一种金属制品表面处理的方法，包括以下步骤：（1）将金属制品用清水洗净，去除不沾粘的杂质，自然晾干；（2）将洗净后的金属制品浸润于高锰酸钾溶液中，持续3~4小时，再将金属制品脱离出高锰酸钾溶液，静置12~24小时；（3）将步骤2处理后的金属制品用稀盐酸进行浸润，控制时间6~8小时；（4）将步骤3处理后的金属制品晾干后，在其表面涂覆一层耐磨剂，利用真空镀膜法进行镀层，得到表面处理完成的金属制品。其中，所述高锰酸钾的水溶液质量浓度不小于60%。其中，所述稀盐酸的质量浓度不大于30%。其中，所述耐磨剂为亚磷酸二正丁酯，涂覆厚度为0.3~0.8mm。有益效果：本专利技术与传统技术相比，通过高锰酸钾的加入使得金属制品表面的亚金属离子氧化，继而加入的酸液清洗电线路杆塔表面形成氯化盐后清除，最后通过耐磨剂与金属制品结合保证了金属制品的表面使用寿命。具体实施方式实施例1：将金属制品用清水洗净，去除不沾粘的杂质，自然晾干；再将金属制品浸润于高锰酸钾溶液中，持续3~4小时，后将金属制品脱离出高锰酸钾溶液，静置12~24小时；接着用稀盐酸浸润金属制品，...
【技术保护点】
1.一种金属制品表面处理的方法，其特征在于，包括以下步骤：（1）将金属制品用清水洗净，去除不沾粘的杂质，自然晾干；（2）将洗净后的金属制品浸润于高锰酸钾溶液中，持续3~4小时，再将金属制品脱离出高锰酸钾溶液，静置12~24小时；（3）将步骤2处理后的金属制品用稀盐酸进行浸润，控制时间6~8小时；（4）将步骤3处理后的金属制品晾干后，在其表面涂覆一层耐磨剂，利用真空镀膜法进行镀层，得到表面处理完成的金属制品。
【技术特征摘要】
1.一种金属制品表面处理的方法，其特征在于，包括以下步骤：（1）将金属制品用清水洗净，去除不沾粘的杂质，自然晾干；（2）将洗净后的金属制品浸润于高锰酸钾溶液中，持续3~4小时，再将金属制品脱离出高锰酸钾溶液，静置12~24小时；（3）将步骤2处理后的金属制品用稀盐酸进行浸润，控制时间6~8小时；（4）将步骤3处理后的金属制品晾干后，在其表面涂覆一层耐磨剂，利用...
【专利技术属性】
技术研发人员：朱德军，
申请(专利权)人：江苏鼎启科技有限公司，
类型：发明
国别省市：江苏,32