一种管路的防水处理方法技术

本发明专利技术公开了一种管路的防水处理方法，包括以下处理步骤：首先将管路外表面上的灰尘和杂质清理掉；使用清水高压冲洗管路外表面，冲洗时间为15‑25分钟，清水温度为25‑45℃；在管路的外表面上涂覆第一层防水涂料，涂覆厚度为0.3‑0.6毫米；然后在外表面上涂覆第二层防水涂料，涂覆厚度为0.4‑0.7毫米，使用热风吹干即可，热风温度为55‑60摄氏度。

A Waterproof Treatment Method for Pipeline

The invention discloses a waterproof treatment method for pipelines, which comprises the following steps: firstly, dust and impurities on the outer surface of pipelines are removed; the outer surface of pipelines is washed by high pressure clean water for 15 25 minutes, and the temperature of clean water is 25 45 C; and the outer surface of pipelines is coated with a first layer of waterproof paint with a thickness of 0.3 0.6 mm; and then the outer surface is washed by high pressure clean water. Coating the second layer of waterproof paint, coating thickness is 0.4 0.7 mm, use hot air to dry, hot air temperature is 55 108

【技术实现步骤摘要】
一种管路的防水处理方法
本专利技术属于工程机械
，具体涉及一种管路的防水处理方法。
技术介绍
管路是指液压系统中传输工作流体的管道，相对于管道而言，管路是一种合理安排的管道系统，因为管路的灵活性，管路常被用于液压系统等靠液体驱动的机械设备。
技术实现思路
为解决现有技术的不足，本专利技术的目的在于提供一种投资成本低，可提高管路的防水性能的管路的防水处理方法。为了实现上述目标，本专利技术采用如下的技术方案：一种管路的防水处理方法，包括以下处理步骤：S1、首先将管路外表面上的灰尘和杂质清理掉；S2、使用清水高压冲洗管路外表面，冲洗时间为15-25分钟，清水温度为25-45℃；S3、在管路的外表面上涂覆第一层防水涂料，涂覆厚度为0.3-0.6毫米；S4、然后在外表面上涂覆第二层防水涂料，涂覆厚度为0.4-0.7毫米，使用热风吹干即可，热风温度为55-60摄氏度。本专利技术的有益之处在于：本专利技术的管路的防水处理方法操作简单，投资成本低，可提高管路的防水性能。具体实施方式以下结合具体实施例对本专利技术作具体的介绍。一种管路的防水处理方法，包括以下处理步骤：S1、首先将管路外表面上的灰尘和杂质清理掉；S2、使用清水高压冲洗管路外表面，冲洗时间为15-25分钟，清水温度为25-45℃；S3、在管路的外表面上涂覆第一层防水涂料，涂覆厚度为0.3-0.6毫米；S4、然后在外表面上涂覆第二层防水涂料，涂覆厚度为0.4-0.7毫米，使用热风吹干即可，热风温度为55-60摄氏度。以上显示和描述了本专利技术的基本原理、主要特征和优点。本行业的技术人员应该了解，上述实施例不以任何形式限制本专利技术，凡采用等同替换或等效变换的方式所获得的技术方案，均落在本专利技术的保护范围内。本文档来自技高网...

【技术保护点】
1.一种管路的防水处理方法，其特征在于，包括以下处理步骤：S1、首先将管路外表面上的灰尘和杂质清理掉；S2、使用清水高压冲洗管路外表面，冲洗时间为15‑25分钟，清水温度为25‑45℃；S3、在管路的外表面上涂覆第一层防水涂料，涂覆厚度为0.3‑0.6毫米；S4、然后在外表面上涂覆第二层防水涂料，涂覆厚度为0.4‑0.7毫米，使用热风吹干即可，热风温度为55‑60摄氏度。

【技术特征摘要】
1.一种管路的防水处理方法，其特征在于，包括以下处理步骤：S1、首先将管路外表面上的灰尘和杂质清理掉；S2、使用清水高压冲洗管路外表面，冲洗时间为15-25分钟，清水温度为25-45℃；...

【专利技术属性】
技术研发人员：宋康，
申请(专利权)人：邳州诚德机械制造有限公司，
类型：发明
国别省市：江苏,32