The invention discloses an anti-corrosion treatment process for ratchet wrench, which comprises the following specific steps: firstly, the wrench is immersed in hot water with a temperature of 45 65 Celsius; the wrench is taken out and put into a heating room with a temperature of 60 70 Celsius; and the wrench is taken out and sprayed with waterproof paint on its outer surface immediately when it is cooled to 30 45 Celsius, and dried by hot air; The outer surface of the hand is sprayed with anticorrosive paint, the thickness of which is 0.2 0.5 mm and dried by hot air; the outer surface of the anticorrosive paint is coated with glycerin layer, and the thickness of which is 0.3 0.4 mm. The finished wrench is obtained.
【技术实现步骤摘要】
一种棘轮扳手用防腐处理工艺
本专利技术属于五金工具
，具体涉及一种棘轮扳手用防腐处理工艺。
技术介绍
棘轮扳手是一种手动螺丝松紧工具，单头、双头多规格活动柄棘轮梅花扳手，是由不同规格尺寸的主梅花套和从梅花套通过铰接键的阴键和阳键咬合的方式连接的，由于一个梅花套具有两个规格的梅花形通孔，使它可以用于两种规格螺丝的松紧，从而扩大了使用范围，节省了原材料和工时费用。活动扳柄可以方便地调整扳手使用角度，这种扳手用于螺丝的松紧操作，具有适用性强，使用方便和造价低的特点。
技术实现思路
为解决现有技术的不足，本专利技术的目的在于提供一种提高了扳手的防水性和防腐性的棘轮扳手用防腐处理工艺。为了实现上述目标，本专利技术采用如下的技术方案：一种棘轮扳手用防腐处理工艺，包括以下具体步骤：S1、首先将扳手浸泡于温度为45-65摄氏度的热水中，浸泡时间为15-20分钟；S2、取出扳手，放入加热房内，加热房的温度为60-70摄氏度，加热时间为0.5-1小时；S3、取出扳手，待其冷却至30-45摄氏度时，立即在其外表面喷涂防水油漆，使用热风吹干，热风的温度为20-45℃；S4、在扳手的外表面喷涂防腐油漆，喷涂厚度为0.2-0.5毫米，使用热风吹干，热风的温度为30-50摄氏度；S5、在防腐油漆层的外表面涂覆甘油层，涂覆厚度为0.3-0.4毫米，得到扳手成品。本专利技术的有益之处在于：本专利技术的棘轮扳手用防腐处理工艺操作简单，工作效率高，提高了扳手的防水性和防腐性。具体实施方式以下结合具体实施例对本专利技术作具体的介绍。一种棘轮扳手用防腐处理工艺，包括以下具体步骤：S1、首先将扳手...
【技术保护点】
1.一种棘轮扳手用防腐处理工艺，其特征在于，包括以下具体步骤：S1、首先将扳手浸泡于温度为45‑65摄氏度的热水中，浸泡时间为15‑20分钟；S2、取出扳手，放入加热房内，加热房的温度为60‑70摄氏度，加热时间为0.5‑1小时；S3、取出扳手，待其冷却至30‑45摄氏度时，立即在其外表面喷涂防水油漆，使用热风吹干，热风的温度为20‑45℃；S4、在扳手的外表面喷涂防腐油漆，喷涂厚度为0.2‑0.5毫米，使用热风吹干，热风的温度为30‑50摄氏度；S5、在防腐油漆层的外表面涂覆甘油层，涂覆厚度为0.3‑0.4毫米，得到扳手成品。
【技术特征摘要】
1.一种棘轮扳手用防腐处理工艺，其特征在于，包括以下具体步骤：S1、首先将扳手浸泡于温度为45-65摄氏度的热水中，浸泡时间为15-20分钟；S2、取出扳手，放入加热房内，加热房的温度为60-70摄氏度，加热时间为0.5-1小时；S3、取出扳手，待其冷却至30-45...
【专利技术属性】
技术研发人员：宋康，
申请(专利权)人：邳州诚德机械制造有限公司，
类型：发明
国别省市：江苏,32