The invention discloses a negative plate for lithium ion batteries and a preparation method thereof. The method comprises: mixing sodium metaborate or its hydrate with metal oxide ball milling to obtain negative active material; mixing conductive agent and negative active material into water-borne binder to obtain negative slurry; coating the negative slurry on negative collector fluid, drying, and obtaining lithium ion electric slurry. Pool negative plate. Before adding metal oxide to binder, the lithium-ion battery negative plate is milled with sodium metaborate or its hydrate. The prepared lithium-ion battery negative plate can greatly improve the cycle stability of charging and discharging of lithium-ion battery negative material, restrain the capacity fluctuation during the long-term cycle of metal oxide negative electrode, and obtain stable capacity and long cycle life.
【技术实现步骤摘要】
一种锂离子电池负极片及其制备方法
本专利技术涉及锂离子电池负极材料领域，具体涉及一种锂离子电池负极片及其制备方法。
技术介绍
随着科技的发展与人类社会的进步，能源枯竭和环境污染问题日益凸显，可再生能源的开发与利用已经成为21世纪人类社会可持续发展的基础。在化学电源中，锂离子电池相对于传统的铅酸电池、镍镉电池、镍氢电池等体系具有能量密度高、自放电率低、循环寿命长、使用温度范围宽、无记忆相应、绿色无污染等优势，已广泛应用于移动通信、笔记本电脑、小型摄像机等电器设备上，在卫星、航空航天以及军事领域也显示了良好的应用前景。尤其近几年来，电动汽车的迅猛发展及电子设备的小型化、轻型化，对锂离子电池提出了更高的要求，开发新型安全高效、高容量、高倍率、长循环寿命的锂离子电池成为目前研究的热点，而发现新的粘结剂以及对现有粘结剂的改性，无论是对正极材料还是负极材料的性能都有很大的提升，也是锂离子电池开发的难点。MxOy+2yLi++2ye-yLi2O+xM许多过渡金属氧化物MxOy(M＝Fe，Co，Ni，Cu，Mo，Gr，Ru)的电极过程都遵循上式所示的转换反应机制，氧化物与金属相之...
【技术保护点】
1.一种锂离子电池负极片的制备方法，其特征在于，包括：(1)偏硼酸钠或其水合物与金属氧化物球磨混合，得到负极活性物质；(2)将导电剂和所述负极活性物质加入至水性粘结剂中混合，得到负极浆料；(3)将所述负极浆料涂布于负极集流体上，烘干，得到锂离子电池负极片。
【技术特征摘要】
1.一种锂离子电池负极片的制备方法，其特征在于，包括：(1)偏硼酸钠或其水合物与金属氧化物球磨混合，得到负极活性物质；(2)将导电剂和所述负极活性物质加入至水性粘结剂中混合，得到负极浆料；(3)将所述负极浆料涂布于负极集流体上，烘干，得到锂离子电池负极片。2.如权利要求1所述的制备方法，其特征在于，所述金属氧化物为过渡金属氧化物或ⅣA族金属氧化物。3.如权利要求2所述的制备方法，其特征在于，所述过渡金属氧化物为Fe2O3、Fe3O4、FeO、NiO、MnO2、MoO、Co3O4、CuO、Cu2O或Cr2O3。4.如权利要求2所述的制备方法，其特征在于，所述ⅣA族金属氧化...
【专利技术属性】
技术研发人员：刘永锋，曲晓雷，潘洪革，高明霞，
申请(专利权)人：浙江大学，
类型：发明
国别省市：浙江,33