An environmentally friendly flame retardant superconducting thermo-UV curable spray adhesive and its processing technology, the present invention relates to the technical field of pressure sensitive adhesives; it consists of 30 to 50 parts of reactive acrylate compounds, 30 to 50 parts of environmentally friendly solvents, 4 to 8 parts of superconductive materials, 10 to 20 parts of environmentally friendly liquid flame retardants and 0.5 to 5 parts of photoinitiator. It has superconductivity, simple process, short reaction time and easy access to raw materials. It can be used in the fields of adding points, car stickers, wall stickers and thermal conductive materials, which greatly increases its application scope and has stronger practicability.
【技术实现步骤摘要】
一种环保阻燃超导热UV固化喷胶及其加工工艺
本专利技术涉及压敏胶
，具体涉及一种环保阻燃超导热UV固化喷胶及其加工工艺。
技术介绍
UV胶又称无影胶、光敏胶、紫外光固化胶，是一种必须通过紫外线光照射才能固化的一类胶粘剂，它可以作为粘接剂使用，也可作为油漆、涂料、油墨等的胶料使用。紫外线(UV)是肉眼看不见的，是可见光以外的一段电磁辐射，波长在10~400nm的范围。无影胶固化原理是UV固化材料中的光引发剂(或光敏剂)在紫外线的照射下吸收紫外光后产生活性自由基或阳离子，引发单体聚合、交联化学反应，使粘合剂在数秒钟内由液态转化为固态。目前的UV固化胶存在着遇明火易燃、贴合附件散热差、涂布不方便等缺陷，局限了其适用范围和使用环境，亟待改进。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足，提供一种结构简单，设计合理、使用方便的环保阻燃超导热UV固化喷胶及其加工工艺，其具有超导热性能，且工艺简易，反应时间短，原料易获取，可用于加点、车贴、墙贴以及导热材料领域，极大地增加了其适用范围，实用性更强。为实现上述目的，本专利技术采用的技术方案是：它由如下重量份成分组...
【技术保护点】
1.一种环保阻燃超导热UV固化喷胶，其特征在于：它由如下重量份成分组成：反应型丙烯酸酯类化合物30‑50份、环保型溶剂30‑50份、超导热材料4‑8份、环保液体型阻燃剂10‑20份、光引发剂0.5‑5份。
【技术特征摘要】
1.一种环保阻燃超导热UV固化喷胶，其特征在于：它由如下重量份成分组成：反应型丙烯酸酯类化合物30-50份、环保型溶剂30-50份、超导热材料4-8份、环保液体型阻燃剂10-20份、光引发剂0.5-5份。2.根据权利要求1所述的一种环保阻燃超导热UV固化喷胶，其特征在于：所述的环保阻燃超导热UV固化喷胶由如下重量份成分组成：反应型丙烯酸酯类化合物40-50份、环保型溶剂40-50份、超导热材料5-8份、环保液体型阻燃剂15-20份、光引发剂1-5份。3.根据权利要求1所述的一种环保阻燃超导热UV固化喷胶，其特征在于：所述的环保阻燃超导热UV固化喷胶由如下重量份成分组成：反应型丙烯酸酯类化合物30-40份、环保型溶剂30-40份、超导热材料4-6份、环保液体型阻燃剂10-15份、光引发剂0.5-3份。4.根据权利要求1所述的一种环保阻燃超导热UV固化喷胶，其特征在于：所述的反应型丙烯酸酯类化合物为聚氨酯丙烯酸酯预聚。5.根据权利要求1所述的一种环保阻燃超导热UV固化喷胶，其特征在于：所述的环保型溶剂为乙醇、醋酸甲酯中的一种或两者混合。6.根据权利要求1所述的一种环保阻燃超导热UV固化喷胶，其特征在于：所述的...
【专利技术属性】
技术研发人员：胡伟，都佩华，
申请(专利权)人：常州都铂高分子有限公司，
类型：发明
国别省市：江苏,32