The invention relates to the technical field of plastic products processing, and specifically discloses a wood-plastic composite pallet, which comprises 30 50 parts of plastic base material, 50 70 parts of modified wood flour, 0.1 2 parts of coupling agent, 0.1 1 part of lubricant, 0.1 1.5 parts of antioxidant and 0.1 1 part of colorant. Modified wood flour is obtained by enzymatic hydrolysis of wood flour with pectinase and cellulase and then immersion in NaOH solution. The wood-plastic composite pallet prepared by the invention has excellent mechanical and mechanical properties and high ecological and economic benefits.
【技术实现步骤摘要】
一种木塑复合材料托盘
本专利技术涉及塑料制品生产
，尤其涉及一种木塑复合材料托盘。
技术介绍
木塑复合材料(WPC)是以木纤维和塑料为主要原料，通过加入各种加工助剂，利用高速混合机混合后，经造粒或直接成型制成的产品。用木塑复合材料制作模压托盘，可以解决木托盘洁净度差、易损坏、寿命短的缺点，也避免了全塑托盘刚性差、价格高、规格灵活性小等缺点，兼有木托盘和全塑托盘的优良特点。随着全球经济的发展和人类生活水平的提高，塑料产品的产量和用量也在日益增长，然而随之而来的“白色污染”对人类生存的地球环境造成了严重的污染，词时也是资源的严重浪费。对“白色污染这类可再生资源进行回收利用，变废为宝的做法符合联合国人类环境组织提出的可持续发展战略的要求。农作物秸秆占作物生物产量的50％左右，是一类及其丰富的可再生有机资源，据中国农科院区划所有关课题组调研分析，我国每年约有6.2亿吨秸秆，这些秸秆大多被白白烧掉，使得大量资源浪费，农业生态平衡破坏，而且污染环境。而且，木材加工厂下脚料木屑、稻壳以及果壳等，若不能得到合理利用，也会造成大量资源浪费，且污染环境。因此如何更好地用废旧塑料...
【技术保护点】
1.一种木塑复合材料托盘，其特征在于，其原料按重量份包括：塑料基料30‑50份、改性木粉50‑70份、偶联剂0.1‑2份、润滑剂0.1‑1份、抗氧剂0.1‑1.5份、着色剂0.1‑1份。
【技术特征摘要】
1.一种木塑复合材料托盘，其特征在于，其原料按重量份包括：塑料基料30-50份、改性木粉50-70份、偶联剂0.1-2份、润滑剂0.1-1份、抗氧剂0.1-1.5份、着色剂0.1-1份。2.根据权利要求1所述的木塑复合材料托盘，其特征在于，所述改性木粉是由木粉经过复合酶制剂酶解后再用NaOH溶液浸泡处理所得。3.根据权利要求1或2所述的木塑复合材料托盘，其特征在于，所述复合酶制剂由果胶酶和纤维素酶按重量比1：6-8组成。4.根据权利要求1-3任一项所述的木塑复合材料托盘，其特征在于，所述木粉是木材加工边角料、秸秆粉、稻糠粉、果壳粉中的一种，其粒径在16mm以下。5.根据权利要求4所述的木塑复合材料托盘，其特征在于，所述改性木粉的制备方法为：将复合酶制剂均匀喷洒在木粉上，控制温度为45-55℃，酶解35-45h后，用浓度为5-10wt％的NaOH溶液浸泡24-36h，之后将木粉洗至中性，再烘干至含水量低于3％，得到改性木粉。6.根据权利要求5所述的木塑复合材料托盘，其特征在于，所述复合酶制剂、木粉、...
【专利技术属性】
技术研发人员：夏则荣，
申请(专利权)人：芜湖亚太通用托盘包装有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。