The invention discloses a new energy-saving composite sealing filler formula, which is characterized by the following components: polytetrafluoroethylene suspended powder 40 50, polypropylene powder 20 30, graphene nanopowder 10 20, organic silicone oil 1 2, PTFE tetrafluoro emulsion 3 5, high-strength glass fiber powder 3 5, toner additives 2 5 and composite additives 10 15. \u3002 The invention has the following advantages: through research, Market Research and repeated use of clinical working conditions, it can thoroughly overcome the defects of traditional sealing fillers in the market, such as poor effect, difficult operation, large maintenance and complex technology.
【技术实现步骤摘要】
一种新型节能复合密封填料配方及其制作工艺
本专利技术涉及工业密封填料及机械密封静环材料
，具体是指一种新型节能复合密封填料配方及其制作工艺。
技术介绍
市场上同类填料(盘根、液体填料、机械密封静环材料等)种类众多，但普遍存在以下不足：1、工艺结构基本为编织工艺或压铸工艺，装拆容易撕裂或断裂，装拆困难；2、产品使用中需要有较大轴向压紧力才可实现抱紧密封，从而会导致密封部位摩擦力巨大，温度较高，需要提供外部冷却液降温，从而增加工艺成本；3、由于为编织工艺，表面呈现微观波纹状，存在大量泄露通道，运行中稍有磨损后，泄露就较为严重，导致现场管理问题较多；4、由于产品本身压缩量较小或使用中会逐步变硬，导致调整次数很少，维护几次后就没有压塑量或压不动了，就要维护换新，从而导致日常维护更换量高居不下；5、市场上厂家、材质种类繁多，质量参差不齐，给业主选型或验收、使用效果带来严重困惑和影响。
技术实现思路
本专利技术要解决的技术问题是克服以上技术问题，提供一种可有效避免传统产品不足，彻底克服市场传统密封填料存在的效果差、操作困难、维护量大、工艺复杂等缺陷的新型节能复合密封填料。为...
【技术保护点】
1.一种新型节能复合密封填料配方，其特征在于：包括以下质量份数成分组成：聚四氟乙烯悬浮微粉40‑50份，聚丙烯微粉20‑30份，石墨烯纳米粉10‑20份，有机硅油1‑2份，PTFE四氟乳液3‑5份，高强玻纤微粉3‑5份，调色添加剂2‑5份和组合助剂10份‑15份。
【技术特征摘要】
1.一种新型节能复合密封填料配方，其特征在于：包括以下质量份数成分组成：聚四氟乙烯悬浮微粉40-50份，聚丙烯微粉20-30份，石墨烯纳米粉10-20份，有机硅油1-2份，PTFE四氟乳液3-5份，高强玻纤微粉3-5份，调色添加剂2-5份和组合助剂10份-15份。2.根据权利要求1所述的一种新型节能复合密封填料配方，其特征在于：所述调色添加剂包括超精石墨微粉、Fe2O3粉和蓝色热固性环氧树脂粉中的其中一种。3.根据权利要求1所述的一种新型节能复合密封填料配方，其特征在于：所述组合助剂包括液体聚硫胶，甲基四氢苯酐，聚丙烯酸钠，脂肪酸，环氧硅烷，烷基甘油醚，聚酰胺，丁氰甲烷，纳米氧化钛和丙烯酸酯。4.一种如权利要求1所述的一种新型节能复合...