The invention relates to the field of metallurgy, in particular to a refractory castable. The invention provides a refractory castable, which comprises the following components: fused corundum 10_5, fused corundum 5_3, fused corundum 3_1, fused corundum 1_0, silicon carbide powder 1_0, silicon carbide powder 200M, alumina powder, spherical asphalt, metal silicon powder, coagulant, metal aluminium powder, organic fiber and powder binder. The main advantage of the refractory castable and the formed iron channel refractory of the present invention is that the high temperature performance of the castable is better, which is mainly due to the formation of mullite phase during the high temperature treatment of the castable, avoiding the liquid phase formed by the reaction between cement and SiO 2, and improving the high temperature performance of the material.
【技术实现步骤摘要】
一种耐火浇注料
本专利技术涉及冶金领域，特别是涉及一种耐火浇注料。
技术介绍
出铁沟作为高炉冶金领域的重要设施，其性能对整体的生产成本有重要的影响。通过改进出铁沟耐材的配方，以提高出铁沟受铁的周期，减少材料的单耗，可以使项目的利益最大化。目前出铁沟浇注料均是采用低水泥浇注料体系，无水泥体系一直是出铁沟乃至整个耐火材料行业的发展方向。目前应用比较广泛，发展比较成熟的就是硅溶胶结合无水泥浇注料。与低水泥浇注料相比，硅溶胶结合无水泥浇注料的主要优点为快干、高温性能好。这主要是由于该类浇注料在高温处理时莫来石相的形成，避免了水泥与SiO2反应形成的液相，提高材料的高温性能。但硅溶胶结合无水泥浇注料同时存在较大的缺陷，例如：生坯强度不足导致脱模和施工问题；其凝结时间受温度和pH值的影响很难满足现场施工条件；硅溶胶是一种水基液体粘合剂，低温条件下的储存、运输和施工具有挑战。这些缺陷很大程度的限制了这种浇注料的大范围使用。
技术实现思路
鉴于以上所述现有技术的缺点，本专利技术的目的在于提供一种耐火浇注料，用于解决现有技术中的问题。为实现上述目的及其他相关目的，本专利技术一方面提供一...
【技术保护点】
1.一种耐火浇注料，按重量百分比计，包括如下组分：
【技术特征摘要】
1.一种耐火浇注料，按重量百分比计，包括如下组分：2.如权利要求1所述的耐火浇注料，其特征在于，所述电熔刚玉中Al2O3含量≥95wt％；和/或，所述碳化硅粉中SiC含量≥97wt％；和/或，所述氧化铝粉中Al2O3含量≥99wt％，所述氧化铝粉的粒度≤2μm。3.如权利要求1所述的耐火浇注料，其特征在于，所述球状沥青的软化点为120℃，粒径为0.2-0.5mm；和/或，所述金属硅粉的Si含量≥97wt％，所述金属硅粉的粒度符合：-200目≥95wt％。4.如权利要求1所述的耐火浇注料，其特征在于，所述促凝剂选自MgO、偏铝酸钠中的一种...
【专利技术属性】
技术研发人员：杨大鹏，
申请(专利权)人：上海宝九和耐火材料有限公司，中冶宝钢技术服务有限公司，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。