A pretreatment method for phosphogypsum, and a paper gypsum board prepared by using the treated phosphogypsum and its preparation method, the phosphogypsum pretreatment method includes mixing the phosphogypsum after drying with the raw lime according to the weight ratio of 100:0.1-3, grinding, calcining at 140-180 degrees C and aging; the paper gypsum board includes 100 weight parts of phosphogypsum, 0.3-1 weight of binder, 0.1-3 weight of lime. The preparation method of paper gypsum board includes mixing pretreated phosphogypsum with other raw materials, mixing to make slurry, forming top and bottom protective paper, drying and cutting according to size. The application realizes the comprehensive utilization of phosphogypsum, and the properties of the prepared paper gypsum board meet the requirements of national standards.
【技术实现步骤摘要】
一种磷石膏的预处理方法和一种纸面石膏板及其制备方法
本申请涉及但不限于新型建筑材料领域，具体涉及但不限于一种纸面石膏板生产用磷石膏的预处理方法和一种纸面石膏板及其制备方法。
技术介绍
磷石膏是磷肥工业的副产物，近年来，中国的磷肥产量和消费量已位居世界第一。随着磷肥产业的迅猛发展，磷石膏的年产量不断增长，到2013年我国的磷石膏年产量已达到了约7000万吨。我国各种工业副产石膏中，磷石膏产量最大，占总量38％。日本、韩国和德国等发达国家对磷石膏的利用率较高，日本达到了90％左右，而我国对磷石膏的利用率才仅有27％。磷石膏的堆积不仅占用了大量的土地资源，而且对周边的大气、土壤、水系及人文环境造成了一定的危害，因此磷石膏的综合利用迫在眉睫。目前，我国生产纸面石膏板的原料大多为脱硫石膏和天然石膏，随着各领域对脱硫石膏的研究和应用日趋成熟，脱硫石膏资源也趋于紧俏。我国的天然石膏资源丰富，但是分布却不均匀，而且高等级的天然石膏的含量并不多，仅8％左右，在我国的大部分地区获得优质的天然石膏非常不容易。与普通天然石膏相比，磷石膏中二水硫酸钙的含量较高，一般为90％左右，从理论上讲...
【技术保护点】
1.一种磷石膏的预处理方法，所述方法包括：将磷石膏烘干后与生石灰按100:0.1～3的重量比混合，研磨，在140～180℃下煅烧，陈化。
【技术特征摘要】
1.一种磷石膏的预处理方法，所述方法包括：将磷石膏烘干后与生石灰按100:0.1～3的重量比混合，研磨，在140～180℃下煅烧，陈化。2.根据权利要求1所述的方法，其中，所述磷石膏与生石灰的重量比为100:0.1～0.6。3.一种纸面石膏板，所述纸面石膏板包括根据权利要求1或2所述的方法预处理的磷石膏。4.根据权利要求3所述的纸面石膏板，其中，所述纸面石膏板的制备原料石膏完全为根据权利要求1或2所述的方法预处理的磷石膏。5.根据权利要求4所述的纸面石膏板，其中，制备所述纸面石膏板的原料包括：6.根据权利要求5所述的纸面石膏板，其中，制备所述纸面石膏板的原料包括：7.根据权利要求5...
【专利技术属性】
技术研发人员：王莹，王鹏起，尹东杰，王丽，谭丹君，何亮，
申请(专利权)人：北新集团建材股份有限公司，
类型：发明
国别省市：北京,11