The invention discloses a preparation process of doped iron borate. The iron salt, manganese salt, titanium salt and borate are mixed evenly in the mixer, and then grinded in the tank mill until the particle size is 300 450 nm to obtain the grinding fine material; the grinding fine material obtained in step (1) is put into the rotary kiln and pre-roasted for 5 7 hours at 400 500 C. The exhaust gas is absorbed by spraying absorption liquid and then roasted at 700 C for 3 small. When calcined, the material is cooled to obtain cooling material, and the cooling material obtained by calcination is broken, screened, removed iron and vacuum packaged to obtain doped iron borate. The preparation process of the doped ferric borate of the invention is simple and low in cost, and the specific surface area is 3_6m.
【技术实现步骤摘要】
一种掺杂型硼酸铁的制备工艺
本专利技术涉及一种掺杂型硼酸铁的制备工艺，属于新能源电池材料领域。
技术介绍
硼酸铁锂(LiFeBO3)作为高容量锂电池阴极材料，理论比容量为220mAh/g,硼酸铁锂理论比容量仅为170mAh/g，更好导电性，极小体积变化率(～2％)。从结构来说，硼酸根(BO3)比(PO4)摩尔质量小(58.8<95)，且硼酸铁锂结构能够同时提供锂离子导电和电子导电。制备这一材料需要十分谨慎，因为一旦和湿气接触，这一材料电化学性能将会快速变差。一般常规的工艺就是采用硼酸铁为前驱体，但是常规的液相合成工艺存在得到的硼酸铁存在比表面积大，且存在结晶水，对合成硼酸铁锂造成不利影响，且合成过程成本高，污水产生量大。
技术实现思路
有鉴于此，本专利技术提供了一种掺杂型硼酸铁的制备工艺，工艺简单，成本低，得到比表面积为3-6m2/g的小比表面无水硼酸铁，一次粒径为400-600nm，且得到掺杂钛与锰的无水硼酸铁。本专利技术通过以下技术手段解决上述技术问题：本专利技术的一种掺杂型硼酸铁的制备工艺，其为以下步骤：(1)将铁盐、锰盐、钛盐与硼酸盐放入混料机内...
【技术保护点】
1.一种掺杂型硼酸铁的制备工艺，其特征在于，为以下步骤：(1)将铁盐、锰盐、钛盐与硼酸盐放入混料机内混合均匀，铁盐、锰盐、钛盐与硼酸盐的摩尔比为1：0.01‑0.02：0.0011‑0.002：1.03‑1.05，然后放入罐磨机内磨细至粒径为300‑450nm得到磨细料；(2)将步骤(1)得到的磨细料放入回转窑中，在温度为400‑500℃下预焙烧5‑7小时，产生的废气经过吸收液喷淋吸收后外排，然后再在温度为650‑700℃焙烧3‑5小时，煅烧得到的物料经过冷却后得到冷却物料；(3)将步骤(2)煅烧得到的冷却物料经行破碎、筛分、除铁和真空包装得到掺杂型硼酸铁。
【技术特征摘要】
1.一种掺杂型硼酸铁的制备工艺，其特征在于，为以下步骤：(1)将铁盐、锰盐、钛盐与硼酸盐放入混料机内混合均匀，铁盐、锰盐、钛盐与硼酸盐的摩尔比为1：0.01-0.02：0.0011-0.002：1.03-1.05，然后放入罐磨机内磨细至粒径为300-450nm得到磨细料；(2)将步骤(1)得到的磨细料放入回转窑中，在温度为400-500℃下预焙烧5-7小时，产生的废气经过吸收液喷淋吸收后外排，然后再在温度为650-700℃焙烧3-5小时，煅烧得到的物料经过冷却后得到冷却物料；(3)将步骤(2)煅烧得到的冷却物料经行破碎、筛分、除铁和真空包装得到掺杂型硼酸铁。2.根据权利要求1所述的一种掺杂型硼酸铁的制备工艺，其特征在于：所述步骤(1)中混料采用斜混...