The invention discloses a heavy metal removal process in the preparation of zinc borate, which is realized by three-stage control of zinc sulfate purification, zinc borate synthesis purification and mother liquor purification, namely, controlling the content of heavy metals introduced by raw zinc sulfate, controlling the distribution proportion of heavy metals in zinc borate, and controlling the content of heavy metals in mother liquor for recycling. By means of three-level control of source removal, process distribution and mother liquor accumulation, the heavy metals in the whole preparation process of zinc borate were removed, the preparation of zinc borate with high quality and low heavy metal content was realized, and the competitiveness of domestic zinc borate in the international market was greatly improved.
【技术实现步骤摘要】
硼酸锌制备过程中的重金属去除工艺
本专利技术涉及一种重金属去除方法，具体涉及一种硼酸锌的制备过程中的重金属去除工艺。本专利技术属于无卤阻燃剂领域。
技术介绍
硼酸锌(Zincborate)是一种环保型的非卤素阻燃剂，根据组成不同(XZnO3·YB2O3·ZH2O)，硼酸锌阻燃剂有十几个品种。最常用的品种为2335型硼酸锌，具有无毒、低水溶性、高热稳定性、分散性好等特性。2335型硼酸锌作为一种高效的阻燃剂，广泛应用于塑料、橡胶加工、交通运输、航天航空、纤维织物、陶瓷釉料、涂料等领域。作为氧化锑或其它卤素阻燃剂的多功能增效添加剂，有效提高阻燃性能，减少燃烧时烟雾的产生，并可以调节橡塑产品的化学，机械，电等方面的性能；作为含卤素等阻燃剂的部分或完全环保替代品，被广泛的直接应用于塑料和橡胶的加工，如PVC、PE、PP、增强聚酰胺、聚氯脂、聚苯乙烯、环氧树脂、聚脂酸乙烯树脂及天然橡胶，苯乙烯丁二烯橡胶、氯丁橡胶等；可以被应用于纸张、纤维织物、装饰板、地板革、壁纸、地毯、陶瓷釉料、杀菌剂、涂料的生产中，以提高阻燃性能。硼酸锌的出口标准中对重金属含量的要求很高，比如欧盟标准要...
【技术保护点】
1.一种硼酸锌制备过程中的重金属去除工艺，其特征在于，主要通过硫酸锌纯化、硼酸锌合成纯化、母液纯化三级控制来实现的，即控制原料硫酸锌引入的重金属含量，控制重金属在硼酸锌中的分布比例，控制循环套用的母液中的重金属含量。
【技术特征摘要】
1.一种硼酸锌制备过程中的重金属去除工艺，其特征在于，主要通过硫酸锌纯化、硼酸锌合成纯化、母液纯化三级控制来实现的，即控制原料硫酸锌引入的重金属含量，控制重金属在硼酸锌中的分布比例，控制循环套用的母液中的重金属含量。2.根据权利要求1所述的一种硼酸锌制备过程中的重金属去除工艺，包括以下步骤：(1)硫酸锌纯化：将硫酸锌溶液加入至反应釜内，控制温度为15-45℃，加入还原性锌粉，搅拌反应5-20min，过滤分离，得到纯化后的硫酸锌溶液可用于合成氢氧化锌；(2)硼酸锌合成纯化：在硼酸-氢氧化锌合成硼酸锌工段，将硼酸加入到反应釜，加入硫酸，搅拌均匀后加入氢氧化锌，升温至95℃反应6h，分离得到低重金属含量的硼酸锌产品及母液；(3)母液纯化：将母液加入至反应釜内，开启搅拌，控制温度为35-55℃，加入还原性锌粉，搅拌反应5-20min，过滤分离，得到纯化后的母液，可循环套用至硼酸锌合成中。3.根...
【专利技术属性】
技术研发人员：冯维春，岳涛，邢文国，陈琦，付永丰，夏学强，苏伟伟，
申请(专利权)人：青岛科技大学，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。