The invention provides a preparation method of thermoplastic resin matrix composites and a method of strengthening anti-collision components of thermoplastic resin matrix composites, in which the preparation method of composites includes: the thermoplastic resin is reinforced with discontinuous fibers to obtain blanks, the surface of continuous fibers is coated with thermoplastic resin to obtain preprepregs, and the billets and prepreprepregs are heated to 170 260 (?) The billet and the preprepreg after heating are quickly laid in the hot-pressing die at 40 80. The die is quickly closed by a hydraulic press and pressed for 20 80 seconds, and the finished product is taken out by opening the die. Through the above technical scheme, the local mechanical properties of the material can be improved without additional forming time.
【技术实现步骤摘要】
热塑性树脂基复合材料的制备和增强防撞构件的方法
本专利技术涉及新材料领域，具体涉及一种热塑性树脂基复合材料的制备和增强防撞构件的方法。
技术介绍
热塑性树脂由于符合汽车行业轻量化和零部件可回收再利用等要求，在汽车生产领域越来越被广泛应用。为了提高热塑性树脂的综合力学性能，采用纤维增强热塑性树脂的方法是目前最常用最有效的手段。纤维增强热塑性树脂基复合材料综合了纤维与热塑性树脂各自的优点，获得单一材料无法达到的优异综合特性，比如优良的力学性能，良好的化学耐蚀性，相对简单的成型工艺和可回收加工性等等。纤维增强热塑性树脂基复合材料的力学性能与纤维的含量密切相关，适当增加纤维含量可以提高复合材料的力学，但是纤维含量越高，复合材料的成型性则相对越差。用于复合材料的纤维可以分为连续纤维与非连续纤维(包括短纤维和长纤维)。连续纤维增强热塑性树脂基复合材料的力学性能高，但是生产成本贵，成型性能也较差；而非连续纤维增强热塑性树脂基复合材料的成型性能较好，成本较低，生产效率高，但力学性能往往不能满足高强度的部件要求。为此，本专利技术应运而生。
技术实现思路
鉴于上述情况，本专利技术旨在于提...
【技术保护点】
1.一种热塑性树脂基复合材料的制备方法，其特征在于，包括以下步骤：将热塑性树脂用非连续性纤维增强得到坯料，将连续纤维表面浸覆热塑性树脂得到预浸料；将所述坯料和所述预浸料加热至170‑260℃；将加热后的所述坯料和所述预浸料迅速铺放于温度为40‑80℃的热压模具内；通过液压机将模具快速合模加压，保压20‑80s后，开模取出成品。
【技术特征摘要】
1.一种热塑性树脂基复合材料的制备方法，其特征在于，包括以下步骤：将热塑性树脂用非连续性纤维增强得到坯料，将连续纤维表面浸覆热塑性树脂得到预浸料；将所述坯料和所述预浸料加热至170-260℃；将加热后的所述坯料和所述预浸料迅速铺放于温度为40-80℃的热压模具内；通过液压机将模具快速合模加压，保压20-80s后，开模取出成品。2.根据权利要求1所述的热塑性树脂基复合材料的制备方法，其特征在于，非连续性纤维增强热塑性树脂的坯料是由挤出机直接在170-260℃高温挤出。3.根据权利要求1所述的热塑性树脂基复合材料的制备方法，其特征在于，所述胚料中所述非连续纤维的质量分数比例范围在20％-40％。4.根据权利要求1所述的热塑性树脂基复合材料的制备方法，其特征在于，所述预浸料中所述连续纤维的质量分数比例范...
【专利技术属性】
技术研发人员：冯浩宇，李彦波，陈梓山，胡淼，陈雨，张展，
申请(专利权)人：凌云工业股份有限公司上海凌云汽车研发分公司，
类型：发明
国别省市：上海,31