The invention discloses a magnesium alloy die casting and a combined surface treatment process for preventing salt spray corrosion. First, the magnesium alloy die casting is treated with the bottom surface of the skin film, then the magnesium alloy die casting is treated with electrophoresis, and then the magnesium alloy die casting after electrophoresis treatment is treated with powder spraying. The invention makes use of the characteristics and advantages and disadvantages of each single surface treatment process and makes a surface combination treatment by sequential reorganization. While satisfying the grounding, shielding and assembling of the whole machine, the problem of preventing galvanic corrosion between magnesium alloy and other metal parts from salt spray corrosion is well solved, and the work is completed. Art is simple.
【技术实现步骤摘要】
镁合金压铸件及其防盐雾腐蚀的表面组合处理工艺
本专利技术涉及一种镁合金压铸件防盐雾腐蚀的表面组合处理工艺，特别是镁合金和其它不同材料金属件装配间发生电偶腐蚀影响正常作业的防盐雾腐蚀的表面组合处理工艺。
技术介绍
现有的镁合金压铸件防盐雾腐蚀的表面处理工艺，主要有：电镀、电泳、烤漆、喷粉、皮膜+喷粉等表面处理工艺。现有表面处理工艺，存在的问题包括：在盐雾要求比较高的装配中，由于镁合金是一种容易被电偶腐蚀的金属，虽然喷粉的隔绝性是比较好，盐雾测试也能达96小时以上，但是零件的喷粉大部分是不能表面全喷，特别是零件间有装配和尺寸公差控制的考虑时，喷粉厚度难以控制，所以装配位和非外观面通常是通过遮喷去保证装配的需求；对于这种情况，现有的表面组合处理方式是喷粉前做皮膜一层做底层处理，皮膜处理由于膜厚和绝缘性不好的问题，虽然在单个零件96小时盐雾测试中腐蚀不太明显，但是当这些没喷粉的位置装配了没做喷粉或没很好绝缘的另一种金属材料零件时，装配间会出现一种电偶腐蚀的现象，会加剧镁合金压铸件的腐蚀。
技术实现思路
为了克服现有技术的不足，本专利技术的目的在于提供镁合金压铸件及其防盐雾腐蚀...
【技术保护点】
1.一种镁合金压铸件防盐雾腐蚀的表面组合处理工艺，其特征在于，包括：皮膜步骤，对镁合金压铸件做皮膜底层表面处理；电泳步骤，对皮膜底层表面处理后的镁合金压铸件做电泳处理；喷粉步骤，对电泳处理后的镁合金压铸件做喷粉处理。
【技术特征摘要】
1.一种镁合金压铸件防盐雾腐蚀的表面组合处理工艺，其特征在于，包括：皮膜步骤，对镁合金压铸件做皮膜底层表面处理；电泳步骤，对皮膜底层表面处理后的镁合金压铸件做电泳处理；喷粉步骤，对电泳处理后的镁合金压铸件做喷粉处理。2.根据权利要求1所述的镁合金压铸件防盐雾腐蚀的表面组合处理工艺，其特征在于，所述电泳步骤，具体为：对皮膜底层表面处理后的镁合金压铸件做阴极电泳处理。3.根据权利要求2所述...
【专利技术属性】
技术研发人员：邓良有，鲍志雄，李钢飞，郑胜平，黄俊铭，
申请(专利权)人：广州市中海达测绘仪器有限公司，
类型：发明
国别省市：广东,44