一种用于酸洗过程中消除氢的试剂，包括以下质量份数的组份：12~42%羟基醋酸、18~95%柠檬酸、10~40%氨基磺酸。本发明专利技术加入到酸槽中，能有效地将镀件表面与酸反应后产生的氢气进行迅速分解。在钢材除锈方面，能更加有效地对钢材表面氧化层进行除锈，有效地抑制了盐酸与钢材反应时的波浪状态。特别是镀过锌的镀件在酸洗过程中，起到安全迅速同时也提供一个安全、环保的生产环境。

Reagent for eliminating hydrogen in pickling process and preparation method thereof

A reagent for removing hydrogen in pickling process includes 12-42% hydroxyacetic acid, 18-95% citric acid and 10-40% aminosulfonic acid. The invention can effectively decompose the hydrogen produced by the reaction of the surface of the plating piece with the acid after being added to the acid tank. In the aspect of steel rust removal, the oxidation layer on the steel surface can be removed more effectively, and the wave state in the reaction of hydrochloric acid with steel can be restrained effectively. Especially the galvanized parts in the pickling process, play a safe and rapid but also provide a safe and environmentally friendly production environment.

【技术实现步骤摘要】
一种用于酸洗过程中消除氢的试剂及其制备方法
本专利技术属于金属表面处理相关
，具体涉及一种用于酸洗过程中消除氢的试剂及其制备方法。
技术介绍
钢铁是日常生活中应用最广泛、用量最大的金属材料，但钢铁的易腐蚀带来巨大的损失。酸洗缓蚀剂可应用于钢铁、电路板、汽车钣金件等金属制品的酸洗工艺中，用以去除金属表面的铁锈、铜锈等氧化物。在现有技术中，通常采用由盐酸、硫酸或者两者复配的混合酸液对金属进行酸洗处理。但是这种技术虽然能够去除金属表面的氧化物，但也能对金属制品造成不必要的严重腐蚀，影响产品质量。在金属表面镀锌是一种提高钢板耐腐蚀性能的有效手段。热镀锌钢板已广泛应用在建材、航空、汽车、家电等不同领域，是我国近几年来产量增长最快的钢材品种之一。我们在日常镀锌中首先要对金属表面的氧化层进行酸洗除锈处理，包括有的产品由于镀锌质量或制作方面的原因需要进退锌后修改等因素都需要进行酸洗处理。金属制品在酸洗过程中进行酸与铁的反应后，产生一定的化学反应，生成了FeCl和水，当酸接触到钢材时，酸槽反映很大，大量HCl气体上升排放，给环境造成一定的影响。如果是退锌产品，就更加麻烦。HCl+Zn化学方程中告本文档来自技高网...

【技术保护点】
1.一种用于酸洗过程中消除氢的试剂，其特征在于，包括以下质量份数的组份： 12~42%羟基醋酸、18~95%柠檬酸、10~40%氨基磺酸。

【技术特征摘要】
1.一种用于酸洗过程中消除氢的试剂，其特征在于，包括以下质量份数的组份：12~42%羟基醋酸、18~95%柠檬酸、10~40%氨基磺酸。2.根据权利要求1所述的一种用于酸洗过程中消除氢的试剂，其特征在于，上述原料的最佳用量为，每升钝化液分别包含：15~35%羟基醋酸、18~46%柠檬酸、10~33%氨基磺酸。3.根据权利要求1所述的一种用于酸洗过程中消除氢的试剂，其特征在于所述羟基醋酸的浓度为22~41℃，柠檬酸的浓度为27~46℃，氨基磺酸的浓度为8~22℃。4.根据权利要求1所述的一种用于酸洗过程中消除氢的试剂的制...