The invention provides a method for preparing Al2O3 ZrO2 hollow microspheres. First, the soluble aluminum salt and zirconium oxychloride were added to the mixed solvent of alcohol and water, sealed at a certain temperature and mixed evenly. Then a certain amount of propylene oxide was added to make it fast sol gel. Finally, the gel was aged in isopropanol and other organic solvents for a long time, and then dried and treated to obtain Al2O3 ZrO2 hollow microspheres. . The method has the advantages of simple process, low cost, good controllability and easy large-scale preparation. The prepared hollow microspheres have large specific surface area, uniform particle size and good dispersion.
【技术实现步骤摘要】
一种Al2O3-ZrO2空心微球的制备方法
本专利技术属于无机功能材料领域，涉及一种Al2O3-ZrO2空心微球的制备方法。
技术介绍
纳米复合材料指由两种或两种以上不同相材料组成，在其复合结构中至少有一个相在一个维度上呈现纳米级别大小。研究发现，对单一物相进行掺杂或者复合可以提高材料的力学性能或者其它性能。因双相或多相复合材料可以兼顾各种单相材料的优点并且可以提高单一相材料的某些性能而备受关注。氧化铝具有较高的热稳定性、较高弹性模量、耐磨和酸碱腐蚀等特性，被广泛应用于人们日常生活中。二氧化锆材料耐火度高，且有很高的室温强度和断裂韧性，广泛应用于特种功能材料领域。两者复合可以有效抑制晶粒的生长和晶型的转变温度，提高烧结程度，从而大大提高材料的力学性能。研究发现单纯的氧化铝空心微球在高温环境下容易发生晶型的转变，特别是1200℃，向α-氧化铝转变过程中，导致了空心微球表面结构发生巨大变化，比表面积剧降，出现了大量大孔，从而使其在高温环境下的应用受到限制。复合后氧化铝对二氧化锆有补强作用，二氧化锆对氧化铝有增韧作用，且对氧化铝在晶型转变温度上有一定的抑制作用，这些“存...
【技术保护点】
1.一种Al2O3‑ZrO2空心微球的制备方法，其特征在于主要步骤如下：步骤一，以铝盐和锆盐为前驱体，以环氧丙烷为促凝剂，在溶剂中采用溶胶‑凝胶制备Al2O3‑ZrO2实心颗粒；步骤二，将Al2O3‑ZrO2实心颗粒通过有机溶剂诱导完成空心化转变，得到Al2O3‑ZrO2空心微球。
【技术特征摘要】
1.一种Al2O3-ZrO2空心微球的制备方法，其特征在于主要步骤如下：步骤一，以铝盐和锆盐为前驱体，以环氧丙烷为促凝剂，在溶剂中采用溶胶-凝胶制备Al2O3-ZrO2实心颗粒；步骤二，将Al2O3-ZrO2实心颗粒通过有机溶剂诱导完成空心化转变，得到Al2O3-ZrO2空心微球。2.一种Al2O3-SiO2空心微球的制备方法，其特征在于主要步骤如下：步骤一，将铝盐和锆盐加入到溶剂中，于40℃-70℃混合均匀；然后加入环氧丙烷使其快速溶胶-凝胶，即得到Al2O3-ZrO2实心颗粒凝胶；步骤二，将Al2O3-ZrO2实心颗粒凝胶在有机溶剂中老化后，经干燥处理得到Al2O3-ZrO2空心微球。3.根据权利要求1或2所述的一种Al2O3-ZrO2空心微球的制备方法，其特征在于步骤二后还包括煅烧处理的步骤，煅烧温度不高于1200℃。4.根据权利要求1或2所述的一种Al2O3-ZrO2空心微球...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。