本发明专利技术公开了一种耐压轻质背衬材料及制备方法，所述背衬材料包括以下质量份数的各组分：环氧树脂80‑100份、增塑剂8‑15份、固化剂5‑10份、稀释剂5‑10份、空心玻璃微珠10‑30份、陶瓷粉80‑100份、氧化铝粉80‑100份、硅烷偶联剂3‑8份。通过合理搭配不同属性的填料和固化剂，提高材料的耐压、耐水、隔声去耦和增大带宽的特性。所得背衬材料可应用于各类高频水声换能器中。

Pressure resistant lightweight backing material and manufacturing method thereof

The invention discloses a pressure-resisting light backing material and a preparation method thereof. The backing material comprises the following components: epoxy resin 80 100, plasticizer 8 15, curing agent 5 10, diluent 5 10, hollow glass beads 10 30, ceramic powder 80 100, alumina powder 80 100, silane. Coupling agent 3, 8. By properly matching different properties of fillers and curing agents, the properties of the material such as pressure resistance, water resistance, sound insulation decoupling and bandwidth increase are improved. The backing material can be applied to all kinds of high frequency underwater acoustic transducers.

【技术实现步骤摘要】
一种耐压轻质背衬材料及制造方法
本专利技术涉及一种适用于高频换能器的耐压轻质背衬材料及制造方法。
技术介绍
海洋是资源和能源的宝库，尤其在深海领域，蕴藏着丰富的各种金属矿产资源、石油、天然气、可燃冰以及深海生物基因资源等。目前，深海勘探、开发主要以深潜技术为基础，利用各类潜器和水下机器人等深海进行观察、测量和取样。高频声纳换能器基阵是各类潜器、水下机器人等深潜装备的主要观测工具，而耐压背衬材料又是高频声纳换能器基阵的关键材料，对高频声纳换能器的耐压极限起决定性作用。背衬材料主要有两大类，一类是高密度的金属为主的材料，耐压强度高，但重量大、成本高，加工不方便。另一类是低密度的发泡材料，主要由聚氨酯泡沫、环氧泡沫或其它发泡塑料，虽然成本低，但是耐压强度低、吸水率高、使用可靠性低。近些年出现了高强度的固体浮力材料，以环氧树脂为粘接剂、大量填充空心玻璃微珠及添加剂复合而成的轻质浮力材料，在高静压使用条件下可取代普通发泡材料。这类高强度的固体浮力材料都为型材，通过机械加工后才可使用，不适用于复杂换能器形状条件下的应用。此外高强度的固体浮力材料密度过低，限制了换能器带宽，对固体浮力材料改性成为适本文档来自技高网...

【技术保护点】
1.一种耐压轻质背衬材料，其特征在于，包括以下质量份数的各组分：

【技术特征摘要】
1.一种耐压轻质背衬材料，其特征在于，包括以下质量份数的各组分：2.根据权利要求1所述的耐压轻质背衬材料，其特征在于，所述塑增塑剂为邻苯二甲酸二丁酯与二甘醇的混合物。3.根据权利要求1所述的耐压轻质背衬材料，其特征在于，所述固化剂为甲基咪唑；所述的硅烷偶联剂为KH560。4.根据权利要求1所述的耐压轻质背衬材料，其特征在于，所述稀释剂为环氧丙烷丁基醚、环氧丙烷苯基醚、三环氧丙烷丙基醚的至少一种。5.根据权利要求1所述的耐压轻质背衬材料，其特征在于，所述空心玻璃微珠的粒径为20μm-300μm。6.根据权利要求1所述的耐压轻质背衬材料，其特征在于，所述陶瓷粉为压电陶瓷粉末，密度2.5g/cm3到4.0g/cm3,粒径50μm-500μm。7.根据权利要求1所述的耐压轻质背衬材料，...