本发明专利技术公开了一种卫浴产品，其特征在于，所述卫浴产品是由空心微珠作为基体填料和热固性树脂组合构成，所述空心微珠按体积比：30‑60％，热固性树脂40‑70％。本发明专利技术还公开了上述卫浴产品的制备方法，通过在上述材料中混合加入市售促进剂、固化剂、偶联功能助剂搅拌制备而成。本发明专利技术具有隔热保温性能好、重量轻，便于移动、节能环保等优点。

A bathroom product and its preparation method

The invention discloses a sanitary ware product, which is characterized in that the sanitary ware product is composed of hollow microspheres as matrix filler and thermosetting resin combination. The hollow microspheres are 30_60% in volume ratio and 40_70% in thermosetting resin. The invention also discloses a preparation method of the sanitary ware product, which is prepared by mixing the said material with a market accelerator, a curing agent and a coupling functional assistant. The invention has the advantages of good heat insulation performance, light weight, easy to move, energy saving and environmental protection.

【技术实现步骤摘要】
一种卫浴产品及其制备方法
本专利技术涉及卫浴产品
，特别是涉及采用轻质材料的卫浴产品

技术介绍
传统的卫浴产品包括浴缸、洗手盘等大都是采用陶瓷烧制而成。其缺点是显而易见的，无论产品及其加工两方面；也有采用亚克力制备的卫浴产品，其重量较陶瓷产品有较大的减少，然后其强度不够，需要另外设置结构支架，上述产品均具有隔热保温效果不佳等多种缺陷。有人采用了独立亚克力浴缸的轻质合模料(其专利申请号为CN201410017090.5)的专利技术专利申请，其公开(公告)号为CN103709699A、申请日为2014.01.15，它至少包括不饱和聚酯树脂DC-191、碳酸钙、颜料糊、促进剂和其他添加剂，还包括玻璃微珠构成的合模料，各组分按重量百分比计为：33％不饱和聚酯树脂DC-191、50％碳酸钙、16％玻璃微珠、1％颜料糊，促进剂量为不饱和聚酯树脂DC-191重量的0.8％，其他添加剂为合模料总重量的0～2％。上述申请还提供了所述轻质合模料的制备方法。上述专利技术所述的轻质合模料重量轻，可以减轻实心合模产品的重量，便于搬运，另外使用玻璃微珠节省了11％的不饱和聚酯树脂和5％的碳酸钙，本文档来自技高网...

【技术保护点】
1.一种卫浴产品，其特征在于，所述卫浴产品是由空心微珠作为基体填料和热固性树脂组合构成，所述空心微珠按体积比：30‑60％，热固性树脂40‑70％。

【技术特征摘要】
1.一种卫浴产品，其特征在于，所述卫浴产品是由空心微珠作为基体填料和热固性树脂组合构成，所述空心微珠按体积比：30-60％，热固性树脂40-70％。2.根据权利要求1所述的卫浴产品，其特征在于，所述热固性树脂为环氧树脂、亚克力树脂、不饱和聚酯树脂之一。3.根据权利要求1所述的卫浴产品，其特征在于，所述热固性树脂中还添加的促进剂、固化剂、偶联功能助剂；促进剂添加量是树脂重量的0.5-5％，固化剂添加量是树脂重量的1-8％，偶联功能助剂添加量是树脂重量的0.5-5％。4.根据权利要求3所述的卫浴产品，其特征在于，所述热固性树脂为环氧树脂采用市售E44型，不饱和树脂采用市售885型；偶联功能助剂为市售KH570型；促进剂采用市售ec-6型；固化剂采用市售m-50型。5.根据权利要求1所述的卫浴产品，其特征在于，所述空心玻璃微珠、空心石英微珠、空心玻纤微珠等不同材质的空心微珠。6.一种权利要求1-5所述的卫浴产品的制备方法，其...

【专利技术属性】
技术研发人员：张贞霞，
申请(专利权)人：张贞霞，
类型：发明
国别省市：广东,44