The invention discloses a preparation method of La-doped Sr_2MnO_4. The steps are as follows: mixing lanthanum nitrate, strontium nitrate, manganese nitrate tetrahydrate and polyethylene glycol, dissolving in citric acid solution at 65 75 C stirring, and continuously stirring to form a viscous gel; the gel is heated to 310 330 C at a rate of 8 min. When no NOx smoke is visible, the sample is ground in an agate bowl after cooling, heated at 670 690 for 6 7 h under nitrogen atmosphere, cooled and grinded, and then heated at 880 890 for 4.5 5.5 H. The method is simple, rapid and easy to operate. The prepared La-doped Sr_2MnO_4 has good catalytic activity and can be prepared on a large scale.
【技术实现步骤摘要】
一种La掺杂的Sr2MnO4的制备方法
本专利技术涉及一种La掺杂的Sr2MnO4的制备方法。
技术介绍
能源的紧缺是目前急需解决的问题，如何以一种高效的清洁能源替代传统的化石能源尤为重要。利用光能，基于模拟自然界中光合作用产生还原型烟酰胺腺嘌呤二核苷酸磷酸（NAPDH）和腺嘌呤核苷三磷酸（ATP），将光子转化为化学能-人工光合作用系统中的光分解水备受人们关注。光水解由两个半反应组成，将质子还原成H2和将水氧化成O2。水氧化是人工光合作用的主要障碍之一。自然中光合过程是通过水氧化络合物实现，包括与多肽协调的四聚体聚集，从而实现在PSⅡ体系中四个电子的转移。最近，水氧化催化剂报道了超过50个异相和均相的光分解水氧化催化剂，其中钙钛矿型异相催化剂占相当大的比例，但是这类材料，引起光电转换率低，并不能被广泛地利用。A2BO4型类钙钛矿氧化物以其离子导电和电子导电的特点，可将染料吸附在介观尺寸的金属氧化物框架中。研究不同程度的掺杂对尖晶石类光催化剂的影响，并通过硫代硫酸钠为电子接受体，从而达到较高的光电转换效率和良好的催化稳定性。不同于ABO3的纳米结构，A2BO4是由A...
【技术保护点】
1.一种La掺杂的Sr2MnO4的制备方法，其特征在于包括如下步骤：将35‑45份硝酸镧、20‑30份硝酸锶、25‑35份硝酸锰四水化合物和5‑15份聚乙二醇混合，在65‑75℃搅拌下溶解于75‑85份柠檬酸溶液中，连续搅拌后形成黏稠的凝胶；将上述凝胶以8℃/min的速率升温至310‑330℃，从而完成硝酸盐分解，当没有NOx烟雾可见时，冷却后在玛瑙研钵中研磨后，将样品在氮气条件下670‑690℃加热6‑7h，冷却和研磨后，将其在880‑890℃下再加热4.5‑5.5h，冷却即得；各原料均为重量份。
【技术特征摘要】
1.一种La掺杂的Sr2MnO4的制备方法，其特征在于包括如下步骤：将35-45份硝酸镧、20-30份硝酸锶、25-35份硝酸锰四水化合物和5-15份聚乙二醇混合，在65-75℃搅拌下溶解于75-85份柠檬酸溶液中，连续搅拌后形成黏稠的凝胶；将上述凝胶以8℃/min的速率升温至310-330℃，从而完成硝酸盐分解，当没有NOx烟雾可见时，冷却后在玛瑙研钵中研磨后，将样品在氮气条件下670-690℃加热6-7h，冷却和...
【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：启东创绿绿化工程有限公司，
类型：发明
国别省市：江苏,32