本发明专利技术公开一种用于电站锅炉化学清洗的漂洗钝化剂及漂洗钝化一步完成工艺，该漂洗钝化剂的质量百分比组成为：乙二胺四乙酸二钠25％～40％、巯基苯并噻唑5％～10％、六偏磷酸钠2％～4％、硫脲2％～5％，余量为水。本发明专利技术漂洗钝化剂组成简单、安全无毒，实施工艺简单，漂洗钝化一步完成，且用量少，漂洗钝化温度低、时间短、环保节能，在金属表面形成的钝化膜优良，适用于盐酸、硫酸、柠檬酸、EDTA钠盐及EDTA氨盐等多种清洗介质。

One step process for rinsing passivating agent and rinsing passivation for chemical cleaning of power plant boilers

The invention discloses a rinsing passivator used for chemical cleaning of utility boilers and a one-step rinsing passivation process. The rinsing passivator consists of 25%-40% disodium ethylenediaminetetraacetate, 5%-10% mercaptobenzothiazole, 2%-4% sodium hexametaphosphate, 2%-5% thiourea, and the remainder is water. The rinsing passivator has the advantages of simple composition, safety and non-toxicity, simple implementation process, one-step rinsing passivation, less dosage, low rinsing passivation temperature, short time, environmental protection and energy saving, excellent passivation film formed on the metal surface, and is suitable for various cleaning media such as hydrochloric acid, sulfuric acid, citric acid, EDTA sodium salt and EDTA ammonium salt.

【技术实现步骤摘要】
一种用于电站锅炉化学清洗的漂洗钝化剂及漂洗钝化一步完成工艺
本专利技术属于电力或化工行业设备的化学清洗
，用于金属表面酸洗后，表面漂洗钝化，具体涉及一种用于电站锅炉化学清洗的漂洗钝化剂及漂洗钝化一步完成工艺。
技术介绍
在跨入21世纪的同时，我国火力发电机组也已进入了1000MW的超超临界机组时代，近年来，新建的机组绝大部分为亚临界、超临界和超超临界机组。随着机组容量的提高，机组结构、设备材质也发生了较大的变化，对受热面清洁度和机组水汽品质的要求更加严格，为获得更加纯净的蒸汽，受热面内壁的清洁度要求也越来越高。热力设备化学清洗是使受热内表面清洁、防止因腐蚀和结垢引起事故的必要技术措施，同时也是提高锅炉热效率、改善机组水汽品质的有效措施之一。新建机组锅炉在投产启动前进行化学清洗，已经作为电站基建安装工程的重要节点，是机组进行点火启动的必备条件之一。电站锅炉化学清洗中的漂洗钝化步骤是关系化学清洗质量的重要一步。电站锅炉经化学清洗、水冲洗、漂洗后，还要进行钝化处理。目前电站锅炉化学清洗漂洗钝化工艺广泛采用的是电力行业标准《火力发电厂锅炉化学清洗导则》(DL/T794-2012)推荐使本文档来自技高网...

【技术保护点】
1.一种用于电站锅炉化学清洗的漂洗钝化剂，其特征在于该漂洗钝化剂由下述质量百分比的原料组成：

【技术特征摘要】
1.一种用于电站锅炉化学清洗的漂洗钝化剂，其特征在于该漂洗钝化剂由下述质量百分比的原料组成：2.根据权利要求1所述的漂洗钝化剂，其特征在于该漂洗钝化剂由下述质量百分比的原料组成：3.一种电站锅炉漂洗钝化一步完成工艺，其特征在于：将化学清洗后的电站锅炉用水冲洗合格，然后向锅炉系统注入去离子水，启动加热器加热，待锅炉系统温度达到65℃～90℃时，向锅炉系统中加入权利要求1所述的漂洗钝化剂，对锅炉进行漂洗钝...