The invention provides an anti radiation concrete active aggregate and a preparation method thereof. An active aggregate for anti-radiation concrete is characterized in that it comprises the following raw materials with the weight fraction of 10_20 phr water, 60_85 phr cement, 10_20 phr barium hydrogen phosphate, 100_130 phr lead powder and 0.1_0.5 phr water reducing agent, and the preparation method is provided, and the raw materials for the anti-radiation concrete prepared by the active aggregate are also provided. Composition: 10 20 phr water, 30 50 phr cement, 20 45 phr active fine aggregate, 65 90 phr active coarse aggregate, 0.1 1 phr water reducer and 2 5 phr fiber; The raw materials used for the active aggregate of the invention are easy to obtain, and can improve the structure density, strength and radiation protection performance of the concrete.
【技术实现步骤摘要】
一种防辐射混凝土活性骨料及其制备方法
本专利技术涉及一种混凝土，尤其涉及一种防辐射混凝土活性骨料及其制备方法。
技术介绍
防辐射混凝土又称防射线混凝土、屏蔽混凝土和原子能防护混凝土，能有效屏蔽原子核反应所产生的γ射线和中子射线。提高混凝土辐射屏蔽所遵循的原则一般是掺入高表观密度和高原子序数材料，如铅粉。但是铅粉无胶凝活性，与水泥相容性差，混凝土中含量低，防辐射效果差。而且铅粉堆积密度远大于普通石子骨料，易造成混凝土离析，施工性能差，易开裂，严重影响核废料的固化安全效果。
技术实现思路
针对以上防辐射混凝土存在的问题，本专利技术提供了一种防辐射混凝土活性骨料及其制备方法。本专利技术的活性骨料所用原料易得，可以提高混凝土的结构致密度、强度和防辐射性能。一种防辐射混凝土活性骨料，包括以下重量分数的原料：10-20份水、60-85份水泥、10-20份磷酸氢钡、100-130份铅粉、0.1-0.5份减水剂。上述活性骨料的制备方法，包括以下步骤：（1）10-20份水、55-75份水泥混合搅拌均匀，然后加入100-130份铅粉，再次搅拌均匀，再加入0.1-0.5份减水剂、1-3份纤...
【技术保护点】
1.一种防辐射混凝土活性骨料，其特征在于，包括以下重量分数的原料：10‑20份水、60‑85份水泥、10‑20份磷酸氢钡、100‑130份铅粉、0.1‑0.5份减水剂。
【技术特征摘要】
1.一种防辐射混凝土活性骨料，其特征在于，包括以下重量分数的原料：10-20份水、60-85份水泥、10-20份磷酸氢钡、100-130份铅粉、0.1-0.5份减水剂。2.一种权利要求1所述的活性骨科的制备方法，其特征在于，包括以下步骤：（1）10-20份水、55-75份水泥混合搅拌均匀，然后加入100-130份铅粉，再次搅拌均匀，再加入0.1-0.5份减水剂、1-3份纤维，混合搅拌5-10min；（2）将步骤（1）的混合物加工成粒状，在3-6MPa和40-60℃条件下一次养护30-70min，得到骨料内芯；（3）将压蒸后的骨料内芯浸水沥干，然后表层包裹5-15...
【专利技术属性】
技术研发人员：宫晨琛，王浩盛，吴波，芦令超，
申请(专利权)人：济南大学，
类型：发明
国别省市：山东,37