The present invention provides a bituminous concrete filler and asphalt concrete, involving the field of engineering materials, made of raw materials of the following weight: 30 ceramic scrap powder, 50 blast furnace slag powder, 4 lime 10, 10 cement 20, twelve alkyl sulfonate 0.4, 0.8, stearic acid 0.2 0.6; the asphalt mixture is mixed. The asphalt concrete is contained in the asphalt concrete. The asphalt concrete is made from the following raw material: 3 bituminous concrete filler, 9 bitumen, 5 bitumen 10, 60 coarse aggregate 70, 20 fine aggregate 30. This invention greatly improves the quality of asphalt concrete by adding asphalt concrete filler. And service life, and waste utilization, turning waste into treasure.
【技术实现步骤摘要】
一种沥青混凝土填料及沥青混凝土
本专利技术涉及工程材料领域，具体涉及一种沥青混凝土填料及沥青混凝土。
技术介绍
沥青混凝土俗称沥青砼，人工选配具有一定级配组成的矿料，碎石或轧碎砾石、石屑或砂、矿粉等，与一定比例的路用沥青材料，在严格控制条件下拌制而成的混合料。虽然填料的用量在沥青混凝土中所占的比重并不大，但是其作为沥青混凝土中的组成成分在决定混合料的性质和状态中起着重要的作用，实验验证，填料的性质对沥青混凝土的高温抗车辙性、低温抗裂性能、抗水害性能及疲劳性能都有着重要影响，不掺加填料的沥青混凝土，经过一段时间的使用后，会出现路面达不到最佳密实度，防水性差，进而导致出现坑槽、松散、脱落的问题，因此对沥青混凝土填料的研究对提升沥青混凝土的使用寿命具有重要意义。
技术实现思路
(一)解决的技术问题针对现有技术的不足，本专利技术提供了一种沥青混凝土填料及沥青混凝土，通过在沥青混凝土中加入沥青混凝土填料，大大提升沥青混凝土的质量和使用寿命，而且废物利用，变废为宝。(二)技术方案为实现以上目的，本专利技术通过以下技术方案予以实现：一种沥青混凝土填料，由以下重量份的原料制成：陶瓷废...
【技术保护点】
1.一种沥青混凝土填料，其特征在于，由以下重量份的原料制成：陶瓷废料粉末30‑50份、高炉矿渣粉5‑15份、石灰4‑10份、水泥10‑20份、十二烷基磺酸钠0.4‑0.8份、硬脂酸0.2‑0.6份。
【技术特征摘要】
1.一种沥青混凝土填料，其特征在于，由以下重量份的原料制成：陶瓷废料粉末30-50份、高炉矿渣粉5-15份、石灰4-10份、水泥10-20份、十二烷基磺酸钠0.4-0.8份、硬脂酸0.2-0.6份。2.如权利要求1所述的沥青混凝土填料，其特征在于，由以下重量份的原料制成：陶瓷废料粉末34-46份、高炉矿渣粉8-12份、石灰6-8份、水泥12-16份、十二烷基磺酸钠0.5-0.6份、硬脂酸0.3-0.5份。3.如权利要求1所述的沥青混凝土填料，其特征在于，由以下重量份的原料制成：陶瓷废料粉末40份、高炉矿渣粉10份、石灰7份、水泥15份、十二烷基磺酸钠0.55份、硬脂酸0.4份。4.如权利要求1所述的沥青混凝土填料，其特征在于，所述陶瓷废料粉末的比表...
【专利技术属性】
技术研发人员：黄龙，许召圣，梁正，孟祥银，
申请(专利权)人：和县祥龙沥青混凝土有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。