一种中等强度细骨料透水混凝土及其用途制造技术

本发明专利技术公开了一种中等强度透水混凝土及其用途，强度等级为C25～C30，由以下重量份的原料制成：水泥74‑108份，矿粉0‑32份，水20‑33份，细骨料309‑343份，外加剂1.00‑1.72份；细骨料的粒径为1.18‑2.36mm。本发明专利技术的混凝土配方中细骨料比表面积较粗骨料比表面积大，能使细骨料与骨料之间的接触点增加，在胶凝材料的胶结作用下提高透水混凝土的强度，同时，增加混凝土的均匀性及表面观感。

Medium strength fine aggregate pervious concrete and use thereof

The invention discloses a medium strength pervious concrete and the use of strength grade of C25 ~ C30, made from the following raw materials in weight portion: 74 cement 108, 0 mineral water 20 32 copies, 33 copies, 343 copies of the 309 fine aggregate, admixture of 1 1.72; fine aggregate size 1.18 2.36mm. The concrete formula of the invention of fine aggregate surface area of coarse aggregate surface area, can make the contact point between fine aggregate and aggregate increase, improve the strength of the pervious concrete, the cementation of cementitious materials and increase the uniformity of concrete and surface impression.

【技术实现步骤摘要】
一种中等强度细骨料透水混凝土及其用途
本专利技术属于建筑材料领域，具体涉及一种中等强度细骨料透水混凝土及其用途，其强度等级为C25～C30。
技术介绍
随着我国新型城镇化建设的发展和水生态环境的恶化，近年我国城市内涝频现，引发了国内对城市水危机的新一轮关注和对传统城市排水系统建设的反思热潮。因此，住房和城乡建设部正式提出了海绵城市的概念，发布相关指南，出台相应的建设政策及计划，旨在改善我国传统城市建设水生态的问题。海绵城市建设已经提上日程，倍受重视。透水混凝土是一种连续孔隙混凝土，具有一定强度的同时还具有透水特性。采用透水混凝土的路面能解决雨水和地下水之间回补和释放，是海绵城市建设的重要途径之一，能够极好地改善地面环境。研究和应用透水混凝土是目前及未来的必然趋势。目前许多研究者纷纷研制出不同类型及强度等级的透水混凝土，透水混凝土工程也不断出现。然而，现有透水混凝土普遍存在原材料成本高、孔隙分布不均匀、强度不高、离散严重，且混凝土面层不美观等缺点，影响了透水混凝土产品的使用和推广。导致上述缺陷的原因有：1、原材料成本高的原因：透水混凝土与普通混凝土的最大区别是连续孔隙，前者连续孔隙率8本文档来自技高网...

【技术保护点】
一种中等强度透水混凝土，其特征在于是由以下重量份的原料制成：

【技术特征摘要】
1.一种中等强度透水混凝土，其特征在于是由以下重量份的原料制成：所述细骨料的粒径为1.18-2.36mm。2.根据权利要求1所述的中等强度透水混凝土，其特征在于：所述的细骨料，石粉含量或含泥量≤2.0％，MB值＜1.0。3.根据权利要求1所述的中等强度透水混凝土，其特征在于：所述的水泥为42.5级以上水泥，其强度富余系数≥...