The invention belongs to the field of building materials, in particular to a concrete. Is composed of the following parts by weight: 100-120 ordinary portland cement, bauxite 80-100, 50-60, 40-50 parts of sand stone, iron powder, sodium sulfite 5-15 powder 3-8 parts, fly ash, 40-50 water reducer 10-20, concrete expansion agent 15-20, Grace 0.5-1, a fiber concrete modifier 10-15 a. The present invention provides concrete, adding gravel and sand can improve the strength of concrete, adding Leigers fiber concrete is not easy to crack, adding expansion agent and water reducing agent, to improve the anti leakage ability of concrete, protection of the certificate of excellent slump and workability and compressive strength, the modifier, the concrete has good dispersion ability and high mechanical properties.
【技术实现步骤摘要】
一种混凝土
本专利技术属于建筑材料领域，具体是一种混凝土。
技术介绍
随着经济的快速发展，我国的建筑业也在迅猛发展，混凝土的使用量也大大增加，但是混凝土在浇筑硬化过程中，由于化学减缩、冷缩和干缩等原因会引起体积收缩。而且单位水泥用量和用水量越多，混凝土体积越大，水分蒸发越快，则收缩越明显。一般情况下，每1m3混凝土收缩值为0.04～0.09％，导致混凝土产生开裂、渗漏、钢筋锈蚀、预应力损失等不良后果。
技术实现思路
为了解决上述问题，本专利技术提供了一种抗压强度大、不易开裂、密度小的混凝土。本专利技术的技术方案如下：一种混凝土，是由以下重量份数的物质组成：普通硅酸盐水泥100-120份、铝矾土80-100份、石子50-60份、砂40-50份、铁粉5-15份、亚硫酸钠粉3-8份、粉煤灰40-50份、减水剂10-20份、混凝土膨胀剂15-20份、格雷斯纤维0.5-1份、混凝土改性剂10-15份。进一步的，一种混凝土，混凝土改性剂是由以下重量份数的物质组成：三元乙丙橡胶5-10份、碳纳米管10-20份、丙烯酸乳液20-35份、炭黑15-25份、二己基丁二酸磺酸钠3-5份、硬脂酸乳酸钠5-10份、阿拉伯树胶5-8份，减水剂为葡萄糖酸钠。本专利技术的有益效果：与现有技术相比，本专利技术提供的混凝土，添加石子和砂可以提高混凝土的强度，添加雷格斯纤维使混凝土不易开裂，添加膨胀剂和减水剂，提高了混凝土的防渗防漏能力，保障了证优异的坍落度、和易性和抗压强度，添加的改性剂，使混凝土具有良好的分散能力以及耐机械性能。具体实施方式实施例1一种混凝土，是由以下重量份数的物质组成：普通硅...
【技术保护点】
一种混凝土，其特征在于，是由以下重量份数的物质组成：普通硅酸盐水泥100‑120份、铝矾土80‑100份、石子50‑60份、砂40‑50份、铁粉5‑15份、亚硫酸钠粉3‑8份、粉煤灰40‑50份、减水剂10‑20份、混凝土膨胀剂15‑20份、格雷斯纤维0.5‑1份、混凝土改性剂10‑15份。
【技术特征摘要】
1.一种混凝土，其特征在于，是由以下重量份数的物质组成：普通硅酸盐水泥100-120份、铝矾土80-100份、石子50-60份、砂40-50份、铁粉5-15份、亚硫酸钠粉3-8份、粉煤灰40-50份、减水剂10-20份、混凝土膨胀剂15-20份、格雷斯纤维0.5-1份、混凝土改性剂10-15份。2.如权利要...
【专利技术属性】
技术研发人员：牟连春，
申请(专利权)人：青岛宏致复合织造有限公司，
类型：发明
国别省市：山东,37