The present invention relates to the treatment of municipal sludge brick manufacturing is a kind of special soil stabilizer resources, the material preparation of brick by soil stabilizer 100 parts by weight of a primary mixture, 5 10 parts by weight of cement and 0.01 0.1 by weight of the composition, the primary mixture consists of 100 portions of the municipal wet sludge, 15 20 weight parts of the lime, and solid waste composition, the soil stabilizer is composed of 100 parts by weight of water, 1 to 15 parts by weight of surface active agent, 0.1 10 parts by weight of boric acid or borate, the solid waste amount of 7 municipal sludge and wet lime mixture the total volume of 13 times. The prepared unburned brick has good compressive strength and water resistance.
【技术实现步骤摘要】
专用土体稳定剂资源化处理市政污泥制造的免烧砖
本专利技术涉及环保领域，具体地，涉及采用专用土体稳定剂资源化处理市政污泥制造的免烧砖。
技术介绍
市政污泥是指城市污水处理厂经浓缩脱水后排出的泥块或泥饼，一般含水率在80%左右，且含有丰富的有机物及N、P、K等营养元素，还含有重金属及病原菌等有害物质，如果处置不当，不仅容易造成环境污染，也会对资源造成浪费。随着我国经济和城市化的快速发展，市政污水的产生及其数量急剧增加。随着城市化的进一步加剧，我国的市政污泥越来越多，急需一种新的工艺与技术，使得市政污泥得到资源化处置。
技术实现思路
为了解决上述问题，本专利技术提供了一种采用专用土体稳定剂资源化处理市政污泥制造的免烧砖，所述免烧砖的制备材料由100重量份的初级混合料、5-10重量份的水泥以及0.01-0.1重量份的土体稳定剂组成，所述初级混合料由100重量份的市政湿污泥、15-20重量份的生石灰、以及固体废弃物组成，所述土体稳定剂由100重量份的水，1-15重量份的表面活性剂，0.1-10重量份的硼酸或硼酸盐组成，所述固体废弃物的用量为市政湿污泥和生石灰混合后的总体积的7-...
【技术保护点】
一种采用专用土体稳定剂资源化处理市政污泥制造的免烧砖，其特征在于，所述免烧砖的制备材料由100重量份的初级混合料、5‑10重量份的水泥以及0.01‑0.1重量份的土体稳定剂组成，所述初级混合料由100重量份的市政湿污泥、15‑20重量份的生石灰、以及固体废弃物组成，所述土体稳定剂由100重量份的水，1‑15重量份的表面活性剂，0.1‑10重量份的硼酸或硼酸盐组成，所述固体废弃物的用量为市政湿污泥和生石灰混合后的总体积的7‑13倍。
【技术特征摘要】
1.一种采用专用土体稳定剂资源化处理市政污泥制造的免烧砖，其特征在于，所述免烧砖的制备材料由100重量份的初级混合料、5-10重量份的水泥以及0.01-0.1重量份的土体稳定剂组成，所述初级混合料由100重量份的市政湿污泥、15-20重量份的生石灰、以及固体废弃物组成，所述土体稳定剂由100重量份的水，1-15重量份的表面活性剂，0.1-10重量份的硼酸或硼酸盐组成，所述固体废弃物的用量为市政湿污泥和生石灰混合后的总体积的7-13倍。2.根据权利要求1所述的一种采用专用土体稳定剂资源化处理市政污泥制造的免烧砖，其特征在于，所述市政湿污泥的含水率为70-85%。3.据权利要求1所述的一种采用专用土体稳定剂资源化处理市政污泥制造的免烧砖，其特征在于，所述水泥为425#普通硅酸盐水泥。4.据权利要求1所述的一种采用专用土体稳定剂资源化处理市政污泥制造的免烧砖，其特征在于，所述土体稳定剂的pH值被调整至8-10。5.据权利要求1所述的一种采用专用土体稳定剂资源化处理市政污泥制造的免...