The invention provides a preparation method of environmental-friendly and heat-insulating composite aerogel material, which comprises the following steps: (1) disposing dopamine hydrochloric acid solution to adjust pH value; (2) adding zirconia fiber felt, high silica fiber and ceramic fiber cotton to soak and oscillate; (3) cleaning after removal and drying the treated mixed fiber; (4) taking chlorine octahydrate. Zirconia and deionized water are mixed to stir solution A; (5) tetraethyl orthosilicate and ethanol are mixed to stir solution B; (6) solution A and solution B are mixed to stir; (7) put into ice water bath, add propylene oxide to stir; (8) add mixed fiber, stir evenly, pour into the mold, seal aging; (9) take out, soak in acetone (10) remove from acetone and dry. The material prepared by this method has very good heat insulation effect, very good mechanical properties, flexural strength, good flexibility, high compressive strength, very good to avoid the sudden fracture of materials.
【技术实现步骤摘要】
一种环保隔热复合气凝胶材料的制备方法
本专利技术涉及一种环保隔热复合气凝胶材料的制备方法。
技术介绍
SiO2气凝胶是目前密度最小及隔热性能最好的新型纳米孔多功能固体材料,在物理化学、热学、光学及电学等领域具有广泛的发展和应用前景。但由于SiO2气凝胶具有极大孔隙率(高达99%)和红外透过率(3~5μm),使其力学性能和中高温隔热性能较差,极大地限制了SiO2气凝胶在各个领域的发展和节能应用。因此改善SiO2气凝胶力学和中高温隔热性能成为国内外的研究热点,而采用纤维复合增强是改善SiO2气凝胶力学性能和隔热性能的最为有效途径。
技术实现思路
要解决的技术问题:本专利技术的目的是提供一种环保隔热复合气凝胶材料的制备方法,所制备的材料热导率很低,具有非常好的隔热效果,同时具有非常好的力学性能,弯曲强度,柔韧性好,压缩强度高,非常好的避免了材料突然断裂的情况。技术方案:一种环保隔热复合气凝胶材料的制备方法,成分按重量份计,包括以下步骤:(1)配置50-80份多巴胺盐酸溶液,调节pH值至9-10;(2)加入5-10份氧化锆纤维毡、1-3份高硅氧纤维和2-5份陶瓷纤维棉,避光浸泡振荡15-20h;(3)取出后用去离子水清洗,在30-40℃下烘干得处理后的混合纤维物;(4)取八水氯氧化锆和去离子水混合,搅拌溶解得溶液A,其中,八水氯氧化锆和去离子水的体积比为1:3;(5)取正硅酸乙酯和乙醇混合,搅拌溶解得溶液B,其中,正硅酸乙酯和乙醇的体积比为3:1;(6)将30-50份溶液A和20-30份溶液B混合,搅拌2-3h;(7)放入冰水浴中,加入3-5份环氧丙烷,搅拌30-40 ...
【技术保护点】
1.一种环保隔热复合气凝胶材料的制备方法,其特征在于:成分按重量份计,包括以下步骤:(1)配置50‑80份多巴胺盐酸溶液,调节pH值至9‑10;(2)加入5‑10份氧化锆纤维毡、1‑3份高硅氧纤维和2‑5份陶瓷纤维棉,避光浸泡振荡15‑20h;(3)取出后用去离子水清洗,在30‑40℃下烘干得处理后的混合纤维物;(4)取八水氯氧化锆和去离子水混合,搅拌溶解得溶液A,其中,八水氯氧化锆和去离子水的体积比为1:3;(5)取正硅酸乙酯和乙醇混合,搅拌溶解得溶液B,其中,正硅酸乙酯和乙醇的体积比为3:1;(6)将30‑50份溶液A和20‑30份溶液B混合,搅拌2‑3h;(7)放入冰水浴中,加入3‑5份环氧丙烷,搅拌30‑40min;(8)加入混合纤维物,搅拌均匀,倒入模具中,密封在50‑55℃下老化24‑27h;(9)取出,浸泡在丙酮中24h,每8h更换一次丙酮;(10)从丙酮中取出,经超临界CO2干燥即得。
【技术特征摘要】
1.一种环保隔热复合气凝胶材料的制备方法,其特征在于:成分按重量份计,包括以下步骤:(1)配置50-80份多巴胺盐酸溶液,调节pH值至9-10;(2)加入5-10份氧化锆纤维毡、1-3份高硅氧纤维和2-5份陶瓷纤维棉,避光浸泡振荡15-20h;(3)取出后用去离子水清洗,在30-40℃下烘干得处理后的混合纤维物;(4)取八水氯氧化锆和去离子水混合,搅拌溶解得溶液A,其中,八水氯氧化锆和去离子水的体积比为1:3;(5)取正硅酸乙酯和乙醇混合,搅拌溶解得溶液B,其中,正硅酸乙酯和乙醇的体积比为3:1;(6)将30-50份溶液A和20-30份溶液B混合,搅拌2-3h;(7)放入冰水浴中,加入3-5份环氧丙烷,搅拌30-40min;(8)加入混合纤维物,搅拌均匀,倒入模具中,密封在50-55℃下老化24-27h;(9)取出,浸泡在丙酮中24h,每8h更换一次丙酮;(10)从丙酮中取出,经超临界CO2干燥即得。...
【专利技术属性】
技术研发人员:何敬堂,庞婉青,
申请(专利权)人:佛山市熙华科技有限公司,
类型:发明
国别省市:广东,44