线材的制程制造技术
The process of wire rod
A process of wire material disclosed in the present invention is the main step of cutting the plural shape memory material after cutting the appropriate length, wrapping the film into at least a line, winding the line on a certain type carrier and fixing the two ends at least one fixed piece, and baking the line for 15 minutes to 25 at a temperature of 175 degrees to 185 degrees. In minutes, it is finalized and placed in cold water for 12 to 18 seconds, and then the line is cooled for 7 minutes to 13 minutes. Finally, the appearance and size of the shape memory materials are confirmed. By the above process, shape memory material is shaped into a predetermined shape to maintain a predetermined shape without external force and can be flexed flexotically at the time of force, and when the external force is relieved, it is highly reduced to a predetermined shape.
【技术实现步骤摘要】
线材的制程
本专利技术提供一种线材的制程，尤指一种有效将形状记忆材料定型为预定造型，并提供形状记忆材料良好的弹性及高度恢复力的线材的制程。
技术介绍
按，在电容器披覆用途等方面所使用的电气绝缘材料，主要系广泛的使用由氯化乙烯所构成的热收缩性套管，但是，聚氯化乙烯制成的热收缩性套管存在有燃烧时会产出氯化氢气体的问题，以及在焚化等废弃处理之际，有容易损害焚化炉等问题点，从此观点出发，遂改用聚酯树脂制之热收缩性套管来取代聚氯化乙烯制之套管。此外，近年来在电容器等电子组件方面，因制品的轻薄短小化而高密度化，故要求可承受电子组件散热的耐热性，因而对聚酯树脂制热收缩性套管仍要求具有良好的耐热性。当使用于铝电解电容器披覆用的情况时，热收缩性聚酯系套管在高温高湿下的耐久性尚嫌不足。例如，汽车的电装组件等乃使用于酷热的车体内或引擎室周围，因而要求高度的耐热性。再者，因为直接受到因风吹雨淋等天候影响、气候变动而发生结露等影响，因而在要求耐热性之同时，亦要求相对应的耐湿性。在此种使用条件下，将热收缩性聚酯系套管披覆的电容器，长期放置于高温高湿下的话，则有迅速变脆弱，而最终将发生龟裂、破...
【技术保护点】
1.一种线材的制程，其特征在于包括步骤如下：(a)将复数形状记忆材料裁切适当长度后，包膜成至少一线扎；(b)将该线扎卷绕于一定型载具上，并以至少一固定件固定该线扎两端；(c)以175度至185度的温度烘烤该线扎15分钟至25分钟，使其定型；(d)将该线扎放置于冷水中12秒至18秒，再对该线扎进行风冷7分钟至13分钟；及(e)对各该形状记忆材料的外观、尺寸进行质量确认。
【技术特征摘要】
1.一种线材的制程，其特征在于包括步骤如下：(a)将复数形状记忆材料裁切适当长度后，包膜成至少一线扎；(b)将该线扎卷绕于一定型载具上，并以至少一固定件固定该线扎两端；(c)以175度至185度的温度烘烤该线扎15分钟至25分钟，使其定型；(d)将该线扎放置于冷水中12秒至18秒，再对该线扎进行风冷7分钟至13分钟；及(e)对各该形状记忆材料的外观、尺寸进行质量确认。2.根据权利要求1所述的线材的制程，其特征在于，所述形状记忆材料为聚氨酯。3.根据权利要求1所述的线材的制程，其特征在于，所述形状...