The present invention discloses a calcareous powder metallurgy material, which is made up of raw material of the following weight percentage: light calcium carbonate 10, calcium stearate 2, three hydroxymethyl propane 0.8, 0.8 acrylamide 1, 2% of acrylamide 1, two benzoyl 0.1 of peroxide, aluminum nitride 3 4%, nickel powder and sortan single oil. The ester 0.1 is 0.4%, Cr10 13%, and the remaining iron. The invention uses acrylamide as a monomer, activates calcium carbonate as the reaction solvent and polymerized under the action of initiator to get the polymer of calcium carbonate modified, and then blend it with aluminum nitride, nickel powder, zinc powder, Cr and iron. The material is well collocated and effectively improves the comprehensive properties of the finished metal material.
【技术实现步骤摘要】
一种钙质粉末冶金材料及其制备方法
本专利技术属于冶金领域，具体涉及一种钙质粉末冶金材料及其制备方法。
技术介绍
现代粉末冶金是一门制造机械零件的先进技术，具有高效、优质、精密、低耗、节能等优点，非常适合于大批量生产各种机械零部件，如汽车零件，尤其是采用铸、锻、机加工等常规方法难以成形或无法成形，以及虽能成形但极不经济的复杂形状零件。采用粉末冶金工艺生产这些零件，不仅可使零件达到高精度、高性能，而且可以保证在流水线上生产的精度和性能的稳定一致，从而给汽车工业乃至现代装备制造业带来了巨大的技术经济效果；目前随着各种设备的动力、速度及负荷在迅速增大，对摩擦材料的要求不断提高。现有的大负载铜基粉末冶金摩擦材料在性能上表现出摩擦系数低、磨损严重、耐热系数低等不足。目前国内外的研究工作多围绕成份对摩擦材料性能的影响、新型摩擦材料开发、烧结工艺改进等方面开展。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足，提供一种钙质粉末冶金材料及其制备方法。为实现上述目的，本专利技术采用以下技术方案：一种钙质粉末冶金材料，它是由下述重量百分比的原料组成的：轻质碳酸钙10-15%、硬...
【技术保护点】
1.一种钙质粉末冶金材料，其特征在于，它是由下述重量百分比的原料组成的：轻质碳酸钙10‑15%、硬脂酸钙2‑3%、三羟甲基丙烷0.8‑1%、丙烯酰胺1‑2%、过氧化二苯甲酰0.1‑0.2%、氮化铝3‑4%、镍粉7‑10%、锌粉2‑4%、山梨坦单油酸酯0.1‑0.4%、Cr10‑13%、剩余的为铁。
【技术特征摘要】
1.一种钙质粉末冶金材料，其特征在于，它是由下述重量百分比的原料组成的：轻质碳酸钙10-15%、硬脂酸钙2-3%、三羟甲基丙烷0.8-1%、丙烯酰胺1-2%、过氧化二苯甲酰0.1-0.2%、氮化铝3-4%、镍粉7-10%、锌粉2-4%、山梨坦单油酸酯0.1-0.4%、Cr10-13%、剩余的为铁。2.一种如权利要求1所述的钙质粉末冶金材料的制备方法，其特征在于，包括以下步骤：（1）取过氧化二苯甲酰，加入到其重量7-9倍的无水乙醇中，搅拌均匀，得引发剂溶液；（2）取轻质碳酸钙、硬脂酸钙混合，升高温度为65-70℃，保温搅拌20-30分钟，加入到混合料重量10-14倍的去离子水中，加入山梨坦单油酸...
【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：繁昌县盛民机械制造有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。