The invention relates to a preparation method of a synthetic gas made of low carbon alcohol molybdenum sulfide catalyst, including the following steps: (1) adding the four hydrate seven ammonium molybdate and thiourea into water according to the molar ratio Mo:S=1:2 4, and then dissolving the solution into a solution A; (2) adding solution A to a hydrothermal reactor and reacting at 220 centigrade, the product is washed and dried. The precipitate A is the petal like MoS2; (3) the A catalyst is prepared by mixing the precipitate A with potassium carbonate according to the molar ratio of Mo:K=1:0.5 ~ (- 1). The catalyst has the advantages of simple preparation method, good sulfur resistance, high selectivity of product total alcohols and C2+ alcohols, and has good industrial application prospects.
【技术实现步骤摘要】
一种用于合成气制低碳醇的硫化钼基催化剂及其制备方法
本专利技术涉及化工催化剂
,具体涉及一种用于合成气制低碳醇的硫化钼基催化剂制备方法和反应条件,尤其是涉及一种以水热合成法制备硫化钼基催化剂。
技术介绍
能源短缺和环境恶化是当前人类面临的重大问题。随着石油资源的日益消耗，开发高效清洁的“绿色能源”不但具有广阔的应用前景，而且具有十分重大的战略意义。其中，经由煤炭或生物质产生合成气制备清洁液体燃料及其他高附加值化学品是能源资源清洁高效利用的重要途径。目前，中国销售的车用乙醇汽油(E10)，即为加入10%（体积分数）变性燃料乙醇调合而成的汽油。受原料供应和生产成本制约，以粮食为原料生产的乙醇无法满足不断增长的工业乙醇和燃料乙醇消费需求。新型非粮乙醇技术，包括醋酸（醋酸酯）加氢制乙醇、纤维素制乙醇、合成气制乙醇等将冲击传统粮食乙醇技术，为乙醇行业带来变革。根据统计，2016年中国汽油的产量为12932万吨。按照国家规定10%添加，燃料乙醇需求为1293.2万吨，考虑生物法乙醇的生产量（年产量200多万吨），合成气制燃料乙醇有约1000万吨的市场空间。中国对燃料乙醇...
【技术保护点】
1.一种合成气制低碳醇硫化钼基催化剂的水热反应制备方法，其特征在于催化剂的组成、制备方法和反应条件。
【技术特征摘要】
1.一种合成气制低碳醇硫化钼基催化剂的水热反应制备方法，其特征在于催化剂的组成、制备方法和反应条件。2.根据权利要求1所述的一种合成气制低碳醇催化剂的水热反应制备方法,其特征在于包括如下步骤:将四水合七钼酸铵和硫脲按照不同比例溶解在水中，溶液经水热反应制得花瓣状MoS2，花瓣状MoS2与碳酸钾按照一定比例机械研磨，烘干后得到非负载型催化剂。3.根据权利要求1和2所述的方法，其特征在于催化剂原料的钼源和硫源。4.其中钼源如钼的含氧酸盐，硫源如硫脲、半胱氨酸、二硫化碳等，钼原子与硫原子的投...
【专利技术属性】
技术研发人员：苏海全，屈皓，李建立，
申请(专利权)人：内蒙古大学，
类型：发明
国别省市：内蒙古,15