The invention relates to an improved PE wall insulation material, which is made up of the following components: polyvinyl chloride resin powder 76, 103 parts, 6 white cotton, 46 parts, 46 sepiolite 7, 8 sepiolite, 8 stabilizers, 8 plaster powder 3, 7 copies of gypsum powder, ethylene vinyl acetate copolymer 12 17, polyphenylene. Propylene 6, 10, lubricant 2, 4, methyl cellulose 0.4, 0.8, foaming agent 3, 12, polyvinyl alcohol 3, 5, and adulterated material 2. The invention has the advantages that the wall insulation material of the invention has good thermal insulation, sound insulation, aseismic and anti leakage performance, and has good economic effect.
【技术实现步骤摘要】
一种改进型聚乙烯墙体保温材料
本专利技术涉及建筑材料领域,特别涉及一种改进型聚乙烯墙体保温材料。
技术介绍
我国每年城乡新建房屋建筑面积近20亿平方米,既有建筑近420亿平方米,建筑能耗已占全国总能耗的27%以上,建筑节能问题已成为我国可持续发展的重要环节,尤其是围护结构的节能具有特别重要的地位。近几年聚苯泡沫板保温便应运而生,聚苯板保温效果非常好,而且密度非常低,能达到100kg/m3以下,但其致命缺陷是易燃,而且燃烧后发烟量大,所以其使用受到极大限制。近年来,北京、上海、沈阳等地发生了因保温层燃烧而引起的“央视大楼”、“上海教师公寓”、“沈阳万鑫酒店”火灾,充分暴露出传统有机保温材料的防火缺陷。住建部也在大力提倡开发新型的阻燃、轻质的保温材料。随着人们对建筑的质量以及美观和舒适度等要求的不断提高,对建筑材料也提出了更高的要求,尤其对墙体保温材料也有了更高的要求。保温材料一般是指导热系数小于或等于0.2的材料,在建筑和工业中采用良好的保温技术与材料,是降低建筑物能耗,延长建筑物使用寿命的有效措施之一。目前国内常见墙体材料的的内使用的墙体材料的导热系数大,有些材料还浪费资源、污染环境,而且施工比较繁琐,保温系统性能有不少缺陷,空鼓、开裂,都是潜在的隐患,其性能不能满足人们的要求。
技术实现思路
本专利技术要解决的技术问题是提供一种具有很好的保温性,隔音、抗震、防渗漏性能好,而且具有良好的经济效果的改进型聚乙烯墙体保温材料。为解决上述技术问题,本专利技术的技术方案为:一种改进型聚乙烯墙体保温材料,其创新点在于:按重量分数配比由以下组分制成:聚氯乙烯树脂粉76-1 ...
【技术保护点】
1.一种改进型聚乙烯墙体保温材料,其特征在于:按重量分数配比由以下组分制成:聚氯乙烯树脂粉76‑103份、白棉6‑12份、包膜玻化微珠43‑46份、海泡石7‑15份、稳定剂5‑8份、石膏粉3‑7份、乙烯—醋酸乙烯共聚物12‑17份、聚苯丙烯6‑10份、内润滑剂2‑4份、甲基纤维素0.4‑0.8份、发泡剂3‑12份、聚乙烯醇3‑5份、掺杂型物质2‑4份。
【技术特征摘要】
1.一种改进型聚乙烯墙体保温材料,其特征在于:按重量分数配比由以下组分制成:聚氯乙烯树脂粉76-103份、白棉6-12份、包膜玻化微珠43-46份、海泡石7-15份、稳定剂5-8份、石膏粉3-7份、乙烯—醋酸乙烯共聚物12-17份、聚苯丙烯6-10份、内润滑剂2-4份、甲基纤维素0.4-0.8份、发泡剂3-12份、聚乙烯醇3-5份、掺杂型物质2-4份。2.根据权利要求1所述的改进型聚乙烯墙体保温材料,其特征在于:所述聚氯乙烯树...