The present invention discloses a graphene / feather composite material and its preparation method. The graphene ethanol dispersions with mass fraction of 0.1 and 10% are inhaled into a disposable syringe, and the feathered feathers are slowly injected into the cavity filled with the interior of the feather shaft, and the wind is dry at 24h at normal temperature. Then the feather was soaked in 60 120min of graphene oxide aqueous solution, washed repeatedly with deionized water and ethanol, and dried naturally. The invention modies the feather with graphene material, and can give the feather certain anti ultraviolet, antibacterial, thermal insulation and mechanical properties.
【技术实现步骤摘要】
一种石墨烯/羽毛复合材料及其制备方法
本专利技术涉及一种石墨烯/羽毛复合材料及其制备方法，属功能材料领域。
技术介绍
羽毛（feather）是禽类表皮细胞衍生的角质化产物。被覆在体表，质轻而韧，略有弹性，具防水性，有护体、保温、飞翔等功能。羽毛中间为空隙，以减轻羽毛的质量。羽毛质轻坚韧，富有弹性和保暖性。我国羽绒和羽毛资源丰富，年产量达60多万吨。目前，除了羽绒被用作保暖填充材料外，其余80％的羽毛纤维只被利用了3％-5％，主要用于填充料、羽毛球及工艺品，少数羽毛纤维被用来提取蛋白质（羽毛重金属吸附/解吸附性能研究进展[J].环境科学与技术,2013,36(03):150-154）。自从2004年英国曼彻斯特大学两位学者发现石墨烯后，由此掀开了石墨烯的研究热潮。石墨烯是由碳原子以sp2杂化轨道形式组成的六角型蜂巢晶格的二维纳米材料，是构成零维富勒烯、一维碳纳米管、三维石墨等碳材料的基本单元。石墨烯是目前世界上最薄的二维材料，拥有极其优异的光、电、力学性能，在光电器件、生物医学材料、吸附材料领域有大量的研究和应用。为了扩大羽毛/羽绒的适用范围，提高羽毛/羽绒制品的附加值，使用纳米材料对羽毛/羽绒进行改性成为研究热点。
技术实现思路
本专利技术提供了一种石墨烯/羽毛复合材料及其制备方法。本专利技术通过下述技术方案予以实现：（1）将质量分数为0.1-10%的石墨烯乙醇分散液吸入到1毫升的一次性注射器内，然后缓慢注射进羽毛的羽轴部位直至充满羽轴内部的空腔，常温下风干24h；（2）将上述羽毛浸渍在质量分数为0.01-10%的氧化石墨烯水溶液中60-120min，使用去离...
【技术保护点】
1.一种石墨烯/羽毛复合材料及其制备方法，其特征在于，步骤一：将石墨烯乙醇分散液吸入到一次性注射器内，然后缓慢注射进羽毛的羽轴部位直至充满羽轴内部的空腔，常温下风干24h；步骤二：将上述羽毛浸渍在氧化石墨烯水溶液中60‑120min，使用去离子水和乙醇反复清洗后，自然风干。
【技术特征摘要】
1.一种石墨烯/羽毛复合材料及其制备方法，其特征在于，步骤一：将石墨烯乙醇分散液吸入到一次性注射器内，然后缓慢注射进羽毛的羽轴部位直至充满羽轴内部的空腔，常温下风干24h；步骤二：将上述羽毛浸渍在氧化石墨烯水溶液中60-120min，使用去离子水和乙醇反复清洗后，自然风干。2.根据权利要求1所述的一种石墨烯/羽毛复合材料的制备方法，其特征...