The invention discloses a feather material based on graphene / nano silver and a preparation method. First, a swallow nest is used as a reducing agent, and graphene / nano silver composite is prepared by one step method. Then the graphene / nanossilver colloid solution is inhaled into a disposable syringe and slowly injected into the feather feathers until it is filled. The cavity inside the shaft is 24h at normal temperature. The invention uses graphene / nano silver composite material to modify feathers to give feathers certain antibacterial, warm and mechanical properties, and does not affect the properties of light, tenacity and elasticity inherent in the feathers.
【技术实现步骤摘要】
一种基于石墨烯/纳米银的羽毛材料及其制备方法
本专利技术属于复合材料领域，特别涉及一种基于石墨烯/纳米银的羽毛材料及其制备方法。
技术介绍
羽毛（feather）是禽类表皮细胞衍生的角质化产物。被覆在体表，质轻而韧，略有弹性，具防水性，有护体、保温、飞翔等功能。羽毛中间为空隙，以减轻羽毛的质量。羽毛质轻坚韧，富有弹性和保暖性。我国羽绒和羽毛资源丰富，年产量达60多万吨。目前，除了羽绒被用作保暖填充材料外，其余80％的羽毛纤维只被利用了3％-5％，主要用于填充料、羽毛球及工艺品，少数羽毛纤维被用来提取蛋白质（羽毛重金属吸附/解吸附性能研究进展[J].环境科学与技术,2013,36(03):150-154）。为了扩大羽毛/羽绒的适用范围，提高羽毛/羽绒制品的附加值，使用纳米材料对羽毛/羽绒进行改性成为研究热点。
技术实现思路
本专利技术针对现有技术存在的不足，旨在提供一种基于石墨烯/纳米银的羽毛材料及其制备方法。本专利技术通过下述技术方案予以实现：（1）将0.01-100g/L的硝酸银水溶液与0.01-100g/L的氧化石墨烯水溶液混合搅拌均匀，所述硝酸银与氧化石墨烯的质量比为1:1-1:10，缓慢加入燕窝，所述燕窝与氧化石墨烯的质量比为2:1-1:2，超声均匀后，置于160-220℃的反应釜中30-600min，取出后用乙醇反复清洗、离心、干燥处理后得到石墨烯/纳米银复合材料；（2）将上述石墨烯/纳米银复合材料重新分散于去离子水中，配制成质量分数为0.01%-10%的石墨烯/纳米银胶体溶液，然后将所述石墨烯/纳米银胶体溶液吸入到1毫升的一次性注射器内，缓慢注射进...
【技术保护点】
1.一种基于石墨烯/纳米银的羽毛材料及其制备方法，其特征在于：步骤一：将0.01‑100g/L的硝酸银水溶液与0.01‑100g/L的氧化石墨烯水溶液混合搅拌均匀，所述硝酸银与氧化石墨烯的质量比为1:1‑1:10，缓慢加入燕窝，超声均匀后，置于160‑220℃的反应釜中30‑600min，取出后用乙醇反复清洗、离心、干燥处理后得到石墨烯/纳米银复合材料；步骤二：将上述石墨烯/纳米银复合材料重新分散于去离子水中，配制成质量分数为0.01%‑10%的石墨烯/纳米银胶体溶液，然后将所述石墨烯/纳米银胶体溶液吸入到一次性注射器内，缓慢注射进羽毛的羽轴部位直至充满羽轴内部的空腔，常温下风干24h。
【技术特征摘要】
1.一种基于石墨烯/纳米银的羽毛材料及其制备方法，其特征在于：步骤一：将0.01-100g/L的硝酸银水溶液与0.01-100g/L的氧化石墨烯水溶液混合搅拌均匀，所述硝酸银与氧化石墨烯的质量比为1:1-1:10，缓慢加入燕窝，超声均匀后，置于160-220℃的反应釜中30-600min，取出后用乙醇反复清洗、离心、干燥处理后得到石墨烯/纳米银复合材料；步骤二：将上述石墨烯/纳米银复合材料重新分散于去离子水中，配制成质量分数为0.01%-10%的...