提高高强度矿用圆环链钢淬透性能的淬火方法技术

本发明专利技术公开了一种提高高强度矿用圆环链钢淬透性能的淬火方法，其工艺为：所述高强度矿用圆环链钢加热到Ac3+10～Ac3+40℃，保温后淬入水中。本方法创新性的降低高强度矿用圆环链钢的淬火温度，在不必对钢的成分进行调整的情况下，显著提高了高强度矿用圆环链钢的淬透性。本方法具有成本低、工艺简单、在生产中容易实施等特点。

Quenching method for improving hardenability of high strength mining round chain steel

The invention discloses a quenching method for improving the hardenability of high strength mining circular chain steel. The process is as follows: the high strength mineral circular chain steel is heated to Ac3+10 ~ Ac3+40 C, and then quenched into water after heat preservation. This method innovatively reduces the quenching temperature of high strength mining circular chain steel, and greatly improves the hardenability of high strength mining circular chain steel without adjusting the composition of steel. The method is characterized by low cost, simple process and easy implementation in production.

【技术实现步骤摘要】
提高高强度矿用圆环链钢淬透性能的淬火方法
本专利技术属于钢铁材料热处理领域，尤其是一种提高高强度矿用圆环链钢淬透性能的淬火方法。
技术介绍
圆环链是采矿设备上的传动部件，具有牵引和导向功能。它的服役环境恶劣、承受载荷大，易发生磨损和疲劳断裂等问题，是设备的关键易损件。为满足新型采矿装备的发展，矿用圆环链的尺寸规格要求变得越来越高。矿用圆环链尺寸规格的增大，要求钢材本身的淬透性要足够高。尤其是圆环链中两个链环相扣的位置，其等效截面尺寸要远远高于圆环链钢钢棒本身。也就是说，圆环链钢棒直径增大一倍，链环相扣位置的等效直径要增大数倍。这容易导致链环的顶部和肩部出现淬不透现象，而这些位置恰恰是圆环链受力最为复杂和恶劣的。因此，保证高的淬透性是制备大规格和超大规格矿用圆环链钢最重要的一个环节。添加硼能显著提高钢的淬透性。但硼的最佳添加量非常少，在实际生产中难以控制，并且硼容易在偏析带聚集，形成硼铁化合物而降低钢的韧性。增加锰含量也会提高钢的淬透性，但锰会增大晶粒增长趋势，对焊缝晶粒尺寸控制不利。其它提高淬透性的元素，镍的价格很昂贵，碳和硅都会降低焊接性能。因此调整合金元素含量来提高高强度矿用圆环本文档来自技高网...

【技术保护点】
1.一种提高高强度矿用圆环链钢淬透性能的淬火方法，其特征在于：所述高强度矿用圆环链钢加热到Ac3+10～Ac3+40℃，保温后淬入水中。

【技术特征摘要】
1.一种提高高强度矿用圆环链钢淬透性能的淬火方法，其特征在于：所述高强度矿用圆环链钢加热到Ac3+10～Ac3+40℃，保温后淬入水中。2.根...

【专利技术属性】
技术研发人员：王振华，齐建军，
申请(专利权)人：河钢股份有限公司，
类型：发明
国别省市：河北,13