The application discloses an antirust agent for the surface of an environment-friendly bending machine, including 75 copies of calcium stearate, 25 nonylphenol polyoxyethylene ether 20, 25 molybdate sodium 95, 25 benzyl oxide amine 80, 20 sulfonate sodium 75, 20 sulfate sulfate, four borate 75, anion surfactant. 70, 10 sodium acetate 80, 2, 3 - two hydrogen ten fluoropentane 25, 55. As a result, the antirust agent has a long time to prevent rust. It can prevent the surface of the material from forming the rust spot again. It is convenient for the disposal of the waste antirust agent. It meets the environmental protection requirements. It has no pollution to the equipment and has no corrosion. It can effectively reduce the production cost and use safety and reliability.
【技术实现步骤摘要】
一种环保型折弯机表面用防锈剂
本专利技术涉及防锈剂,尤其涉及一种环保型折弯机表面用防锈剂。
技术介绍
目前,国内大型机加工零件在安装前及中途运输过程中大都需要防锈处理,现在普遍采用牛油或普通的防锈油进行防锈,这些防锈剂虽然具有一定的防锈作用,但是效果不佳。
技术实现思路
本专利技术的目的提供一种环保型折弯机表面用防锈剂,解决上述现有技术问题中的一个或者多个。根据本专利技术的一个方面,提供一种环保型折弯机表面用防锈剂,按重量份数包括硬脂酸钙15-75份,壬基酚聚氧乙烯醚20-60份,钼酸钠25-95份,烷基苄氧化胺25-80份,磺酸钠20-75份,硫酸钡20-75份,四硼酸钾25-80份,阴离子型表面活性剂15-70份,醋酸钠10-80份,2,3—二氢十氟戊烷25-55份。在一些实施方式中:按重量份数包括硬脂酸钙45份,壬基酚聚氧乙烯醚40份,钼酸钠70份,烷基苄氧化胺55份,磺酸钠45份,硫酸钡45份,四硼酸钾55份,阴离子型表面活性剂40份,醋酸钠45份,2,3—二氢十氟戊烷40份。生产时,将上述物料全部加入搅拌桶内,加热到100℃,搅拌均匀,然后冷却,即可制成产品。本专利技术的防锈剂防锈时间较长,使用后能够防止材料表面再次形成锈斑;便于废弃防锈剂的处理排放,符合环保要求,对设备无污染,无腐蚀,有效降低生产成本,使用安全可靠。具体实施方式实施例1:按重量份数包括硬脂酸钙15份,壬基酚聚氧乙烯醚20份,钼酸钠25份,烷基苄氧化胺25份,磺酸钠20份,硫酸钡20份,四硼酸钾25份,阴离子型表面活性剂15份,醋酸钠10份,2,3—二氢十氟戊烷25份。实施例2:按重 ...
【技术保护点】
一种环保型折弯机表面用防锈剂,其特征在于:按重量份数包括硬脂酸钙15‑75份,壬基酚聚氧乙烯醚20‑60份,钼酸钠25‑95份,烷基苄氧化胺25‑80份,磺酸钠20‑75份,硫酸钡20‑75份,四硼酸钾25‑80份,阴离子型表面活性剂15‑70份,醋酸钠10‑80份,2,3—二氢十氟戊烷25‑55份。
【技术特征摘要】
1.一种环保型折弯机表面用防锈剂,其特征在于:按重量份数包括硬脂酸钙15-75份,壬基酚聚氧乙烯醚20-60份,钼酸钠25-95份,烷基苄氧化胺25-80份,磺酸钠20-75份,硫酸钡20-75份,四硼酸钾25-80份,阴离子型表面活性剂15-70份,醋酸钠10-80份,2,3—二氢十...