This application has disclosed an environment-friendly antirust agent for gear use, including 15 titanium dioxide, 55 copies of titanium white powder, 20 sodium silicate of sodium silicate, 40 copies of acrylic resin 5, 10 sodium gluconate 60, 70 sodium sulfonate, 70 bauxite, 15 phosphoric acid, sodium silicate, acetate base acetate The state silica is 10, 75, and 10 boric acid, 70 copies. As a result, the antirust agent has a long time to prevent rust. It can prevent the surface of the material from forming the rust spot again. It is convenient for the disposal of the waste antirust agent. It meets the environmental protection requirements. It has no pollution to the equipment and has no corrosion. It can effectively reduce the production cost and use safety and reliability.
【技术实现步骤摘要】
一种环保型齿轮用防锈剂
本专利技术涉及防锈剂,尤其涉及一种环保型齿轮用防锈剂。
技术介绍
目前,国内大型机加工零件在安装前及中途运输过程中大都需要防锈处理,现在普遍采用牛油或普通的防锈油进行防锈,这些防锈剂虽然具有一定的防锈作用,但是效果不佳。
技术实现思路
本专利技术的目的提供一种环保型齿轮用防锈剂,解决上述现有技术问题中的一个或者多个。根据本专利技术的一个方面,提供一种环保型齿轮用防锈剂,按重量份数包括钛白粉15-55份,三聚硅酸钠20-66份,丙烯酸树脂5-40份,葡萄糖酸钠10-60份,磺酸钠24-70份,铝矾土15-80份,磷酸三钠10-65份,1,2-二乙氧基硅酯基乙烷20-45份,胶态二氧化硅10-75份,硼酸10-70份。在一些实施方式中:按重量份数包括钛白粉32份,三聚硅酸钠45份,丙烯酸树脂25份,葡萄糖酸钠33份,磺酸钠55份,铝矾土60份,磷酸三钠40份,1,2-二乙氧基硅酯基乙烷35份,胶态二氧化硅33份,硼酸30份。生产时,将上述物料全部加入搅拌桶内,加热到100℃,搅拌均匀,然后冷却,即可制成产品。本专利技术的防锈剂防锈时间较长,使用后能够防止材料表面再次形成锈斑;便于废弃防锈剂的处理排放,符合环保要求,对设备无污染,无腐蚀,有效降低生产成本,使用安全可靠。具体实施方式实施例1:按重量份数包括钛白粉15份,三聚硅酸钠20份,丙烯酸树脂5份,葡萄糖酸钠10份,磺酸钠24份,铝矾土15份,磷酸三钠10份,1,2-二乙氧基硅酯基乙烷20份,胶态二氧化硅10份,硼酸10份。实施例2:按重量份数包括钛白粉32份,三聚硅酸钠45份,丙烯酸树脂 ...
【技术保护点】
1.一种环保型齿轮用防锈剂,其特征在于:按重量份数包括钛白粉15‑55份,三聚硅酸钠20‑66份,丙烯酸树脂5‑40份,葡萄糖酸钠10‑60份,磺酸钠24‑70份,铝矾土15‑80份,磷酸三钠10‑65份,1,2‑二乙氧基硅酯基乙烷20‑45份,胶态二氧化硅10‑75份,硼酸10‑70份。
【技术特征摘要】
1.一种环保型齿轮用防锈剂,其特征在于:按重量份数包括钛白粉15-55份,三聚硅酸钠20-66份,丙烯酸树脂5-40份,葡萄糖酸钠10-60份,磺酸钠24-70份,铝矾土15-80份,磷酸三钠10-65份,1,2-二乙氧基硅酯基乙烷20-45份,胶态二氧化硅10-75份...