The aim of the invention is to provide a polyamide PA6 reinforced modified material without affecting the mechanical properties of the material and improving the mechanical properties of the polyamide material and a preparation method thereof. The physical and chemical properties of polyamide PA6 are similar to nylon 66, however, the melting point of polyamide is low, and the temperature range of the process is very wide. Its impact resistance and solubility are better than that of PA66, but its hygroscopicity is stronger. Because many quality characteristics of plastic parts are affected by hygroscopicity, the design of products with polyamide PA6 should take full account of this. The polyamide PA6 reinforced material modified by the invention greatly improves the mechanical strength of the material and enables it to be better applied.
【技术实现步骤摘要】
聚酰胺PA6增强改性材料
本专利技术属尼龙PA6材料生产
，提高聚酰胺材料的机械特性，生产出符合社会需求的产品。
技术介绍
聚酰胺PA6的化学物理特性和尼龙66很相似，然而，它的熔点较低，而且工艺温度范围很宽。它的抗冲击性和抗溶解性比PA66要好,但吸湿性也更强。因为塑件的许多品质特性都要受到吸湿性的影响，因此使用聚酰胺PA6设计产品时要充分考虑到这一点。
技术实现思路
本专利技术的目的是提供一种不影响材料的力学性能，提高聚酰胺材机械特性的聚酰胺PA6增强改性材料及其制备方法。所述聚酰胺PA6增强改性材料由下列重量比原料组成：聚酰胺PA6原料：65～75无碱玻璃纤维：25～35硅烷偶联剂(KH-550):1.5～2.5玻璃相容剂：1.5～2.5抗氧剂(乙烯-辛烯的共聚物)：0.5～1.5所诉聚酰胺PA6增强改性材料制备方法包括以下步骤：将上述各种原料在高速混合器中干混15-20分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为160-180℃，二区为230-250℃，三区为255-275℃，四区为250-270℃；五区为230-250℃，停留时间为1-2分钟，压力为10-15Mpa。具体实施方式下面通过具体实施方式对本专利技术做进一步的说明，以下实施例仅是对本专利技术进行说明而非对其加以限定。实施例1：(1)按重量比分分别称取各原料如下：聚酰胺PA6原料：65无碱玻璃纤维：25硅烷偶联剂(KH-550):1.5玻璃相容剂：1.5抗氧剂(乙烯-辛烯的共聚物)：0.5(2)将上述各种原料在高速混合器中干混15-20分...
【技术保护点】
一种聚酰胺PA6增强改性材料，其特征在于，由下列重量比原料组成：聚酰胺PA6原料：65～75无碱玻璃纤维：25～35硅烷偶联剂(KH‑550):1.5～2.5玻璃相容剂：1.5～2.5抗氧剂(乙烯‑辛烯的共聚物)：0.5～1.5。
【技术特征摘要】
1.一种聚酰胺PA6增强改性材料，其特征在于，由下列重量比原料组成：聚酰胺PA6原料：65～75无碱玻璃纤维：25～35硅烷偶联剂(KH-550):1.5～2.5玻璃相容剂：1.5～2.5抗氧剂(乙烯-辛烯的共聚物)：0.5～1.5。2.根据权利要求1所述的聚酰胺PA6增强改性材料，其特征在于，最优重量比原料组成为：聚酰胺PA6原料：70无碱玻璃纤维：30硅烷偶联剂(KH-550)：2.0玻璃相容剂：2.0抗...
【专利技术属性】
技术研发人员：丁磊，
申请(专利权)人：青岛绿谷生物科技有限公司，
类型：发明
国别省市：山东,37