The invention discloses a temperature resistant capacitor plastic shell, which relates to the technical field of capacitor, and is made of the following components: ABS resin, polyethylene resin, chloroprene rubber, two pentaerythritol phosphite two ISO ester, urea, talc powder, stearic acid, six methylene four amine, electrohydrolysis glass fiber, alkyd resin, and polymer. The nano sericite, six methyl two silanane and plasticizer are coated with ethylene wax, mercapto, and silica. The invention is based on ABS resin as the main basic component, adding a variety of other auxiliary components and after a reasonable ratio, it improves the problem of weak comprehensive performance stored in the traditional ABS capacitor plastic shell, and the processing has been processed. The characteristics are better.
【技术实现步骤摘要】
一种耐温变电容器塑料外壳
本专利技术属于电容器
，具体涉及一种耐温变电容器塑料外壳。
技术介绍
现有的电力电容器外壳通常采用金属或ABS工程塑料制成。前者壳体笨重，且成本高，易生锈，又极易产生壳体击穿和拉火现象，正逐渐被ABS材料所替代。而ABS材料壳体虽然重量轻，但是这种材料制成的壳体的壁厚必须在5cm以上，否则抗变形温度低，易变形，但是壁太厚时，加工难度增大，生产时废品多，合格率低，增大了生产成本，同时ABS材料易吸水，导致电容器壳体绝缘性能降低，抗电强度下降。随着电力电容器技术的发展，其电荷容量、负荷逐渐增大，随之而来的就是温度、强度、噪声等问题，2002年的国际大电网会议曾指出换流变电站的电力电容器噪声高达105dB，而且电容器工作温度变化，致使壳体强度等性能下降，影响了其使用寿命。
技术实现思路
本专利技术的目的是针对现有的问题，提供了一种耐温变电容器塑料外壳。本专利技术是通过以下技术方案实现的：一种耐温变电容器塑料外壳，按重量份计由以下成分制成：ABS树脂98-110、聚乙烯树脂5-8、氯丁橡胶2-5、二亚磷酸季戊四醇酯二异葵酯1-4、尿素0.3-0...
【技术保护点】
一种耐温变电容器塑料外壳，其特征在于，按重量份计由以下成分制成：ABS树脂98‑110、聚乙烯树脂5‑8、氯丁橡胶2‑5、二亚磷酸季戊四醇酯二异葵酯1‑4、尿素0.3‑0.5、滑石粉4‑6、硬脂酸1.5‑1.8、六亚甲基四胺2‑5、电解改性玻璃纤维5‑8、醇酸树脂4‑10、聚乙烯蜡2‑6、巯基丙烯酸酯1‑5、二氧化硅包覆的纳米绢云母4‑6、六甲基二硅氮烷0.3‑0.5、增塑剂0.8‑1.2。
【技术特征摘要】
1.一种耐温变电容器塑料外壳，其特征在于，按重量份计由以下成分制成：ABS树脂98-110、聚乙烯树脂5-8、氯丁橡胶2-5、二亚磷酸季戊四醇酯二异葵酯1-4、尿素0.3-0.5、滑石粉4-6、硬脂酸1.5-1.8、六亚甲基四胺2-5、电解改性玻璃纤维5-8、醇酸树脂4-10、聚乙烯蜡2-6、巯基丙烯酸酯1-5、二氧化硅包覆的纳米绢云母4-6、六甲基二硅氮烷0.3-0.5、增塑剂0.8-1.2。2.如权利要求1所述的一种耐温变电容器塑料外壳，其特征在于，所述聚乙烯树脂为线性低密度聚乙烯树脂。3.如权利要求1所述的一种耐温变电容器塑料外壳，其特征在于，所述滑石粉粒度为1250目。4.如权利要求1所述的一种耐温变电容器塑料外壳，其特征在于，所述电解改性玻璃纤维制备方法为：配制电解液，将尿素按15g：300mL的比例添加到质量分数为1.53%的氯化铈...