The invention discloses a modified acrylonitrile butadiene styrene copolymer copolymer with small low temperature brittleness. Its raw material is composed of 140 copies of acrylonitrile acrylonitrile butadiene styrene copolymer 100, 60 portions of polytetrafluoroethylene 40, 6 tert butyl peroxide 4, 1 (two methylamino) phenol 1, 2 copies of silane, and 2 copies of silane. Coupling agent KH 570, 4.5 portions, 15 hollow glass beads, 10 vermiculite powder, 18 portions, 6 mica powder 6, 12 barium sulfate, 20, polyurethane rubber 10, calcium sulfate, sodium sorate, sodium sulfonate. The modified acrylonitrile styrene acrylonitrile styrene copolymer has good low temperature brittleness, good aging resistance, high structural strength and high impact strength, and is suitable for automotive parts.
【技术实现步骤摘要】
一种低温脆性小的改性丙烯腈-丁二烯-苯乙烯共聚物
本专利技术涉及塑料
，尤其涉及一种低温脆性小的改性丙烯腈-丁二烯-苯乙烯共聚物。
技术介绍
丙烯腈-丁二烯-苯乙烯共聚物(ABS树脂)具有高韧性、尺寸稳定性、化学稳定性、热稳定性及润滑特性等优点，适合制作汽车车身板、汽车侧面护板、挡泥板、汽车门框等、齿轮箱、汽车保险杠以及要求具有抗化学反应和耐腐蚀性、热稳定性、抗冲击性以及几何稳定性的产品。但是ABS树脂塑料合金其韧性会受到温度很大的影响，一般表现为低温脆性，因此对塑料进行改性，提高其耐低温性能，以拓宽塑料应用领域。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种低温脆性小的改性丙烯腈-丁二烯-苯乙烯共聚物，低温脆性好，耐老化效果好，而且结构强度高，抗冲击强度高，适用于汽车领域配件。本专利技术提出的一种低温脆性小的改性丙烯腈-丁二烯-苯乙烯共聚物，其原料按重量份包括：丙烯腈-丁二烯-苯乙烯共聚物100-140份，聚四氟乙烯40-60份，二叔丁基过氧化氢4-6份，2,4,6-三(二甲氨基甲基)苯酚1-2份，硅烷偶联剂KH-5702.5-4.5份，中空...
【技术保护点】
一种低温脆性小的改性丙烯腈‑丁二烯‑苯乙烯共聚物，其特征在于，其原料按重量份包括：丙烯腈‑丁二烯‑苯乙烯共聚物100‑140份，聚四氟乙烯40‑60份，二叔丁基过氧化氢4‑6份，2,4,6‑三(二甲氨基甲基)苯酚1‑2份，硅烷偶联剂KH‑570 2.5‑4.5份，中空玻璃微珠15‑25份，蛭石粉10‑18份，云母粉6‑12份，沉淀硫酸钡12‑20份，聚氨酯橡胶10‑18份，山梨酸钙4‑8份，十二烷基苯磺酸钠4‑8份。
【技术特征摘要】
1.一种低温脆性小的改性丙烯腈-丁二烯-苯乙烯共聚物，其特征在于，其原料按重量份包括：丙烯腈-丁二烯-苯乙烯共聚物100-140份，聚四氟乙烯40-60份，二叔丁基过氧化氢4-6份，2,4,6-三(二甲氨基甲基)苯酚1-2份，硅烷偶联剂KH-5702.5-4.5份，中空玻璃微珠15-25份，蛭石粉10-18份，云母粉6-12份，沉淀硫酸钡12-20份，聚氨酯橡胶10-18份，山梨酸钙4-8份，十二烷基苯磺酸钠4-8份。2.根据权利要求1所述低温脆性小的改性丙烯腈-丁二烯-苯乙烯共聚物，其特征在于，丙烯腈-丁二烯-苯乙烯共聚物、聚四氟乙烯的重量比为110-130：45-55。3.根据权利要求1所述低温脆性小的改性丙烯腈-...