The invention discloses a climate aging 125 degree thermoplastic polyolefin cable material, which consists of 80 parts of polypropylene resin, 10~20 copies of polyethylene resin, 5~10 compatibilizer, 1~5 compound antioxidant, 1~3 surface treatment agent and 5~10 black mother; in which the polypropylene resin is a isotactic polypropylene resin and inlay. A mixture of polypropylene resin with a proportion of (40~60) (40~20); the compound antioxidant is a mixture of liquid antioxidant and powder antioxidant; the cable material provided by the invention is resistant to weather aging, high temperature resistance grade and recyclability, and can replace the existing weatherability of 125 degree irradiated crosslinking materials and 90 degree high density polyethylene. Material Science\u3002
【技术实现步骤摘要】
一种耐气候老化125度热塑性聚烯烃电缆料及其制备方法
本专利技术涉及电缆及其制备领域，具体涉及一种耐气候老化125度热塑性聚烯烃电缆料及其制备方法。
技术介绍
对于户外电缆来说，耐气候老化是非常重要的一项指标，它决定了电缆的使用寿命，现有的耐气候老化多为90度耐温等级的高密度聚乙烯材料和125度辐照交联聚烯烃材料，前者的耐温等级较低，不能满足电流量日趋增加的需求；后者为不可回收材料，使用寿命到期后不能降解回收，对环境造成污染，因此，研究一种耐温等级更高的热塑性聚烯烃材料已迫在眉睫。
技术实现思路
针对现有耐气候老化存在的安全隐患和问题，本专利技术的目的之一在于提供一种耐温等级达到125度，可回收的热塑性聚烯烃材料；本专利技术的目的之二在于解决耐候聚乙烯材料耐温等级较低的问题；本专利技术的目的之三在于提供一种耐气候老化125度热塑性聚烯烃材料的制备方法。为了达到上述目的，本专利技术采用如下的技术方案：一种耐气候老化125度热塑性聚烯烃电缆料，由以下重量份的原料制备而成：在本专利技术的一个优选实施例中，所述聚丙烯树脂为等规聚丙烯树脂和嵌段聚丙烯树脂的混合物，质量比为40～...
【技术保护点】
一种耐气候老化125度热塑性聚烯烃电缆料，其特征在于，由以下重量份的原料制备而成：
【技术特征摘要】
1.一种耐气候老化125度热塑性聚烯烃电缆料，其特征在于，由以下重量份的原料制备而成：2.如权利要求1所述的一种耐气候老化125度热塑性聚烯烃电缆料，其特征在于，所述聚丙烯树脂为等规聚丙烯树脂和嵌段聚丙烯树脂的混合物，质量比为40～60：40～20。3.如权利要求1所述的一种耐气候老化125度热塑性聚烯烃电缆料，其特征在于，所述聚乙烯树脂为线性低密度聚乙烯，融指范围0.5～2g/10min，分子量15万到30万。4.如权利要求1所述的一种耐气候老化125度热塑性聚烯烃电缆料，其特征在于，所述相容剂为马来酸酐接枝线性低密度聚乙烯、马来酸酐接枝聚丙烯、马来酸酐接枝高密度聚乙烯中的一种或任意两种以上的混合。5.如权利要求1所述的一种耐气候老化125度热塑性聚烯烃电缆料，其特征在于，所述复配抗氧剂为液体抗氧剂和粉体抗氧剂的混合物，其中所述液体抗...
【专利技术属性】
技术研发人员：怀宝祥，宋刚，李现春，
申请(专利权)人：上海至正道化高分子材料股份有限公司，
类型：发明
国别省市：上海,31