The invention discloses a kind of polypropylene material with high impact strength for automobile. Its raw material includes 100 portions of polypropylene 80, 6 chloroprene rubber, 14 copies of chloroprene rubber, 20 chloro sulfonated polyethylene 10, 4 crosslinking agent, 65 filling agent, 65 titanate coupling agent, 4 copies of titanate coupling agent, 4 copies of tar oil, antioxidant, 2 lubricants 4 copies. The filling and reinforcing agent is made up of bentonite complex 20, 30 parts, glass fiber 6, 14, sepiolite powder 10, 16, talcum powder 8, 12. The bentonite composite was prepared by the following process: mixing N dehydroabir abietic acid, nano bentonite and epoxy soybean oil acrylate. The bentonite was heated and stirred with the addition of 1,1 (tert butyl peroxide) cyclohexane, and the bentonite complex was heated and stirred.
【技术实现步骤摘要】
一种汽车用高抗冲击强度的聚丙烯材料
本专利技术涉及汽车
，尤其涉及一种汽车用高抗冲击强度的聚丙烯材料。
技术介绍
虽然目前汽车上使用的塑料种类很多，但聚丙烯塑料占有较大比重。聚丙烯塑料的密度小、价格低、无毒、耐腐蚀性优越、易加工成型等优点，并且具有良好的机械性能，尤适于在汽车领域应用。但聚丙烯塑料存在抗冲击强度差的缺点，亟待解决。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种汽车用高抗冲击强度的聚丙烯材料，硬度较高，不仅热稳定性，而且拉伸强度与韧性极好，同时抗冲击效果好，具有不易变形、不生锈、抗冲击强度高的优点。本专利技术提出的一种汽车用高抗冲击强度的聚丙烯材料，其原料按重量份包括：聚丙烯80-100份，氯丁橡胶6-14份，氯磺化聚乙烯10-20份，交联剂2-4份，填充补强剂55-65份，钛酸酯偶联剂2-4份，松焦油2-4份，防老剂2-4份，润滑剂2-4份。优选地，防老剂按重量份包括：防老剂BLE1-2份，防老剂RD2-4份。优选地，填充补强剂按重量份包括：膨润土复合物20-30份，玻璃纤维6-14份，海泡石粉10-16份，滑石粉8-12份。优...
【技术保护点】
一种汽车用高抗冲击强度的聚丙烯材料，其特征在于，其原料按重量份包括：聚丙烯80‑100份，氯丁橡胶6‑14份，氯磺化聚乙烯10‑20份，交联剂2‑4份，填充补强剂55‑65份，钛酸酯偶联剂2‑4份，松焦油2‑4份，防老剂2‑4份，润滑剂2‑4份。
【技术特征摘要】
1.一种汽车用高抗冲击强度的聚丙烯材料，其特征在于，其原料按重量份包括：聚丙烯80-100份，氯丁橡胶6-14份，氯磺化聚乙烯10-20份，交联剂2-4份，填充补强剂55-65份，钛酸酯偶联剂2-4份，松焦油2-4份，防老剂2-4份，润滑剂2-4份。2.根据权利要求1所述汽车用高抗冲击强度的聚丙烯材料，其特征在于，防老剂按重量份包括：防老剂BLE1-2份，防老剂RD2-4份。3.根据权利要求1或2所述汽车用高抗冲击强度的聚丙烯材料，其特征在于，填充补强剂按重量份包括：膨润土复合物20-30份，玻璃纤维6-14份，海泡石粉10-16份，滑石粉8-12份。4.根据权利要求3所述汽车用高抗冲击强度的聚丙烯材料，其特征在于，膨润土复合物采用如下工艺制备：将N-脱氢枞基丙烯酰胺、...
【专利技术属性】
技术研发人员：刘仕明，
申请(专利权)人：全椒祥瑞塑胶有限公司，
类型：发明
国别省市：安徽,34