一种中空珊瑚状四氧化三钴纳米粒子的制备方法技术
Preparation method of hollow coral four oxidized three cobalt nanoparticles
The preparation method of hollow coral like four oxide three cobalt nanoparticles is mainly to dissolve cobalt salt and structure guide in a mixed solution of ethanol and water, and then add ammonia water to agitation for 2 ~ 30h at normal temperature. After the reaction, the product is obtained by separation, washing and drying, and the obtained product is calcined at 250~700. Finally, hollow coral like four oxidized three cobalt nanoparticles were obtained. The preparation process of the invention is simple, the whole process is carried out under normal temperature and atmospheric pressure without any complex equipment. It is a simple, efficient, inexpensive, environmentally friendly, and easy to scale preparation method.
【技术实现步骤摘要】
一种中空珊瑚状四氧化三钴纳米粒子的制备方法
本专利技术属于金属材料
，特别涉及一种纳米粒子的制备方法。
技术介绍
Co3O4属于立方晶系，其中氧原子包围着Co(Ⅱ)离子四面体和Co(Ⅲ)离子八面体，晶体场稳定化能较高。四氧化三钴被广泛应用于催化剂、磁性半导体、气体传感器元件、锂离子电池材料、超级电容器材料等重要领域。由于物质的微观形貌与一些宏观性质有很大的关系，因此近年来，合成不同形貌结构的四氧化三钴材料已经成为科研工作者关注的热点问题，目前被合成出来的四氧化三钴形貌类型有很多，例如纳米线、纳米棒、纳米管、纳米立方体、空心球、花状微球等。中空结构由于具有其独特的开放式结构和较高的比表面积，可以提供较多的表面活性位点，因此，四氧化三钴中空结构在超级电容器和多相催化剂领域等中具有较好的应用前景，成为四氧化三钴材料的研究热点。目前，合成中空结构的四氧化三钴的方法有很多，例如，刘勇等人用葡萄糖为模板专利技术了一种中空高比表面积的四氧化三钴(刘勇，付孝锦，郑小刚，董立春.一种高比表面空心结构四氧化三钴及其合成方法和应用.中国：CN106348349.[P]2018.0...
【技术保护点】
一种中空珊瑚状四氧化三钴纳米粒子的制备方法，其特征在于：其包括如下步骤：(1)将乙醇与水混合形成溶液，将钴盐和结构导向剂溶于乙醇与水的溶液中，形成混合溶液；(2)在上述混合溶液中加入氨水，氨水加入完毕后不断搅拌2～30h；(3)搅拌反应结束后通过分离、洗涤和干燥得到产物，将所得产物在250～700℃下进行焙烧得到中空珊瑚状四氧化三钴纳米粒子。
【技术特征摘要】
1.一种中空珊瑚状四氧化三钴纳米粒子的制备方法，其特征在于：其包括如下步骤：(1)将乙醇与水混合形成溶液，将钴盐和结构导向剂溶于乙醇与水的溶液中，形成混合溶液；(2)在上述混合溶液中加入氨水，氨水加入完毕后不断搅拌2～30h；(3)搅拌反应结束后通过分离、洗涤和干燥得到产物，将所得产物在250～700℃下进行焙烧得到中空珊瑚状四氧化三钴纳米粒子。2.根据权利要求1所述的中空珊瑚状四氧化三钴纳米粒子的制备方法，其特征在于：所述的钴盐为醋酸钴、硝酸钴、氯化钴或硫酸钴，所述结构导向剂为抗坏血酸(VC)。...
【专利技术属性】
技术研发人员：陈玲，张楠，王晓爽，陈祥成，郑伟超，李翡，尹娟娟，
申请(专利权)人：燕山大学，
类型：发明
国别省市：河北,13