The invention discloses a kind of alcohol solid fuel and a preparation method thereof, belonging to the solid fuel technology field. This alcohol solid fuel consists of the following raw materials: 90~110 industrial alcohol, 2~3 stearic acids, 1~5 sodium hydroxide solutions, 1~3 zine stearate and 0.1 to 1 ferrocene; the quality of the industrial alcohol is above 95%, and the sodium hydroxide solution is sodium hydroxide with a mass of 10 to 20%. Water solution. This alcohol solid fuel is made by mixing raw materials in a certain order at a certain temperature. This solid alcohol fuel has the characteristics of high combustion value, stable combustion process, long storage time, low cost and easy preparation.
【技术实现步骤摘要】
一种醇类固体燃料及其制备方法
本专利技术涉及一种固体燃料及其制备方法，具体涉及一种醇类固体燃料及其制备方法。
技术介绍
随着生活水平不断提高，人们出去吃火锅、烤鱼、烤肉、自助餐的频率越来越高。目前在餐馆用餐时需要用到加热的燃料一般包括气体(如煤气、燃气)、液体酒精和固体酒精。由于气体燃料和液体酒精在使用过程中的危险性较大，近年来出现过各种安全事故，所以在用餐过程的使用中逐渐被固体酒精取代，因此固体酒精的需求量日益增多。为满足这一社会需求，国内市场上有各种固体酒精出售。但是，目前市场上的固体酒精中，有的含有硝酸酯(或盐)，有的含胺类物质或含有氯或硫、磷等物质，燃烧后会产生含氯硫、磷或重金属元素等的有害气体，对人体健康极为不利。有的制备工艺较复杂，且操作不方便，成本较高。有的要添加昂贵的化工原料，从而使产品成本偏高。有的固体酒精中含有较高量的纤维素酯，在燃烧后排放出的气体中仍含有较高的(NO)x，污染环境，影响身体健康。同时，固体酒精还存在的普遍问题是燃烧热值低，燃烧稳定性不好，燃烧持续时间不长、保存时间不长等。在制备固体酒精时通常存在固化剂添加量的控制问题。如果固化...
【技术保护点】
一种醇类固体燃料，其特征在于，由下述重量份数的原料组成：工业酒精90～110份，硬脂酸2～3份，氢氧化钠溶液1～5份，硬脂酸锌1～3份，二茂铁0.1～1份；所述工业酒精的质量浓度为95％以上，所述氢氧化钠溶液为质量浓度为10～20％的氢氧化钠水溶液。
【技术特征摘要】
1.一种醇类固体燃料，其特征在于，由下述重量份数的原料组成：工业酒精90～110份，硬脂酸2～3份，氢氧化钠溶液1～5份，硬脂酸锌1～3份，二茂铁0.1～1份；所述工业酒精的质量浓度为95％以上，所述氢氧化钠溶液为质量浓度为10～20％的氢氧化钠水溶液。2.如权利要求1所述的醇类固体燃料，其特征在于，由下述重量份数的原料组成：工业酒精100～105份，硬脂酸2～3份，氢氧化钠溶液2～3份，硬脂酸锌2～3份，二茂铁0.1～0.5份。3.如权利要求2所述的醇类固体燃料，其特征在于，由下述重量份数的原料组成：工业酒精102份，硬脂酸3份，氢氧化钠溶液3份，硬脂酸锌2份，二茂铁0.3份。4.如权利要求1所述的醇类固体燃料，其特征在于：所述氢氧化钠溶液的质量浓度为15％，由工业烧碱和水制成。5.一种权利要求1所述的醇类固体燃料的制备方法，其特征在于，包括如下步骤：(1)按重量份数将硬脂酸加入工业酒...
【专利技术属性】
技术研发人员：林天华，
申请(专利权)人：柳州市金升汽车配件有限公司，
类型：发明
国别省市：广西,45
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。