The invention is about a new type of fire retardant coating. According to the weight ratio, the components of the new type of fire retardant coating include 60 inorganic hollow filler, 20 adhesives, 30 copies, 20 ammonium polyphosphate 30, 40 film forming agent 50, 40 foaming agent 50 copies, and 1 synergist 10. The coating is a green environmental protection coating. The coating not only has the characteristics of long refractory time, good decorative performance, good adhesion and water resistance, but also adopts an independent raw material selection method, making the coating free of APEO, without lead or chromium and other metal compounds, and will not cause harm to the environment and human health.
【技术实现步骤摘要】
一种新型防火涂料
本专利技术属于涂料领域，具体涉及一种新型防火涂料。
技术介绍
随着人们安全意识的增加，新型防火涂料的应用越来越广泛。但是对于新型防火涂料的研制，仍存在着很多技术难点，需要解决的主要问题是提高耐水性、缩短干燥时间、延长耐火时间、提高储存稳定性、增加装饰性等。综上所述，目前市场上的室内薄型钢结构新型防火涂料耐水性差，储存稳定性差，耐火时间短，干燥时间长，装饰性差等缺点。因此研究开发性能优异、环境友好的新型防火涂料是室内钢结构防火保护的必然趋势。
技术实现思路
为了解决现有技术中存在的问题，本专利技术提供了一种提高新型防火涂料的耐水性能和改善涂层粘结性的新型防火涂料。本专利技术的目的及解决其技术问题是采用以下技术方案来实现的。依据本专利技术提出的一种新型防火涂料，按照重量份配比，所述防火涂料的组分包括：无机空心填料60-70份、粘合剂20-30份、聚磷酸铵20-30份、成膜剂40-50份、发泡剂40-50份以及增效剂1-10份。与现有技术相比，本专利技术所提供的一种新型防火涂料具有如下优点：该涂料属于绿色环保性涂料，该涂料不仅具有耐火时间长，装饰性能好，粘结性好、耐水性优等特点，还采用独立的原材料选取方法，使涂料不含APEO，不含铅或铬等金属化合物，不会对环境及人类健康造成危害。具体实施方式为更进一步阐述本专利技术为达成预定专利技术目的所采取的技术手段及功效，以下结合较佳实施例，对依据本专利技术提出的一种新型防火涂料其具体特征及其功效，详细说明如后。实施例1一种新型防火涂料，按照重量份配比，所述防火涂料的组分包括：无机空心填料60份、粘合剂20份、...
【技术保护点】
一种新型防火涂料，其特征在于：按照重量份配比，所述新型防火涂料的组分包括：无机空心填料60‑70份、粘合剂20‑30份、聚磷酸铵20‑30份、成膜剂40‑50份、发泡剂40‑50份以及增效剂1‑10份。
【技术特征摘要】
1.一种新型防火涂料，其特征在于：按照重量份配比，所述新型防火涂料的组分包括：无机空心填料60-70份...
【专利技术属性】
技术研发人员：王红超，贾留宽，
申请(专利权)人：洛阳神佳窑业有限公司，
类型：发明
国别省市：河南,41