The invention relates to the technical field of polymer materials, in particular to a wear-resistant rubber for basketball inner liner. This kind of basketball internal bladder is made of wear-resistant rubber as follows: polyurethane rubber 35~55 portion, 12~25 portion of nitrile rubber, silicone rubber 10~18, four ethyl orthosilicate 5~12, 4~9 part of wear-resistant carbon black, nano Zinc Oxide 2~6 portion, 1~8 portion of carbon fiber, 1~7 part of phthalic acid two butyl ester, and sulfurized alkyl phenol calcium 3~10. Parts, 5~10 content of propane siloxane, 7~12 of pine tar, 5~13 of carrageenan, 1~5 of chlorinated paraffin and 11~19 of curing accelerator. The wear-resistant rubber material used in the basketball internal bladder is cheap, easy to get, low production cost, good wear resistance, corrosion resistance, antioxidation, good elasticity, not easy to damage, and long service life.
【技术实现步骤摘要】
一种篮球内胆用耐磨橡胶
本专利技术涉及高分子材料
，具体涉及一种篮球内胆用耐磨橡胶。
技术介绍
篮球运动是一项普及程度非常高的运动，老少皆宜，而且场地要求也不高，篮球本身的材质在很大程度上决定了篮球的寿命，其弹性、外形也会对比赛的竞技程度、成绩和观赏性带来很大的影响。篮球的内胆多使用橡胶材料制成，现有橡胶材料比较容易损坏，弹性较差，无法满足人们的使用需求。
技术实现思路
本专利技术目的在于解决上述问题，提供了一种篮球内胆用耐磨橡胶。为实现上述目的，本专利技术提供了一种篮球内胆用耐磨橡胶，由如下按照重量份的原料组成：聚氨酯橡胶35~55份、丁腈橡胶12~25份、有机硅橡胶10~18份、正硅酸四乙酯5~12份、耐磨炭黑4~9份、纳米氧化锌2~6份、碳纤维1~8份、邻苯二甲酸二丁酯1~7份、硫化烷基酚钙3~10份、丙二烯硅氧烷5~10份、松焦油7~12份、卡拉胶5~13份、氯化石蜡1~5份和硫化促进剂11~19份。所述篮球内胆用耐磨橡胶，由如下按照重量份的原料组成：聚氨酯橡胶40~50份、丁腈橡胶15~20份、有机硅橡胶13~16份、正硅酸四乙酯8~11份、耐磨炭黑5...
【技术保护点】
一种篮球内胆用耐磨橡胶，其特征在于，由如下按照重量份的原料组成：聚氨酯橡胶35~55份、丁腈橡胶12~25份、有机硅橡胶10~18份、正硅酸四乙酯5~12份、耐磨炭黑4~9份、纳米氧化锌2~6份、碳纤维1~8份、邻苯二甲酸二丁酯1~7份、硫化烷基酚钙3~10份、丙二烯硅氧烷5~10份、松焦油7~12份、卡拉胶5~13份、氯化石蜡1~5份和硫化促进剂11~19份。
【技术特征摘要】
1.一种篮球内胆用耐磨橡胶，其特征在于，由如下按照重量份的原料组成：聚氨酯橡胶35~55份、丁腈橡胶12~25份、有机硅橡胶10~18份、正硅酸四乙酯5~12份、耐磨炭黑4~9份、纳米氧化锌2~6份、碳纤维1~8份、邻苯二甲酸二丁酯1~7份、硫化烷基酚钙3~10份、丙二烯硅氧烷5~10份、松焦油7~12份、卡拉胶5~13份、氯化石蜡1~5份和硫化促进剂11~19份。2.根据权利要求1所述的篮球内胆用耐磨橡胶，其特征在于，由如下按照重量份的原料组成：聚氨酯橡胶40~50份、丁腈橡胶15~20份、有机硅橡胶13~16份、正硅酸四...