裂纹聚沫析晶釉釉料制备及其制备方法技术

本发明专利技术公开了一种裂纹聚沫析晶釉，裂纹聚沫析晶釉的各组分和各组分质量如下：马迹泥50份～60份；方解石6份～8份；氧化锌6份～8份；碳酸锂10份～12份；高岭土3份～5份；硅酸锆10份～12份；该釉在1270℃倒焰窑氧化气氛中烧制而成，该釉呈透明状，具有极细腻的裂纹，裂纹中有气泡，有白色的晶体，釉体表面光滑，该釉使艺术性较强的釉，适合内销市场，符合国内客户的审美。

Preparation and preparation method of cracked foam glazed glaze

The invention discloses a kind of crack polycrystalline glaze, and the components and components of the crack polycrystalline glaze are as follows: 50 to 60 copies of trace mud, 6 to 8 calcite, 6 to 8 Zinc Oxide, 10 to 12 of lithium carbonate, 3 to 5 of the kaolin and 10 to 12 of zirconium silicate, and the glaze is burned in the oxidizing atmosphere of 1270 centigrade furnace kiln. The glaze is transparent and has a very delicate crack. There are bubbles in the crack, white crystal and smooth surface of the glaze. The glaze makes the artistic glaze suitable for the domestic market, which is in line with the aesthetic of domestic customers.

【技术实现步骤摘要】
裂纹聚沫析晶釉釉料制备及其制备方法
本专利技术涉及一种裂纹聚沫析晶釉制作及其制备方法，属于釉料领域。
技术介绍
该釉的研发是通过对坯釉膨胀系数不断调节，并结合结晶釉工艺，不断交叉测试，不断调整，该釉呈透明状，具有极细腻的裂纹，裂纹中有气泡，有白色的晶体，釉体表面光滑，该釉使艺术性较强的釉，适合内销市场，符合国内客户的审美。
技术实现思路
本专利技术所要解决的技术问题是克服现有技术的不足，调节裂纹的程度，控制白色晶体的产生，本专利技术公开了一种裂纹聚沫析晶釉，该釉的各组分和各组分质量如下：马迹泥50份～60份；方解石6份～8份；氧化锌6份～8份；碳酸锂10份～12份；高岭土3份～5份；硅酸锆10份～12份；所述的裂纹聚沫析晶釉制作方法，该方法的步骤如下：a按照各组份和各组份质量份备料；b)按料：釉料:球:水＝1:1.6:0.6，湿法球磨12～14小时，球磨后的釉料过200目筛后，调制成53～54波美浓度，取干净坯体浸全色釉；c)将浸好釉的坯体放入倒焰窑以1270℃氧化气氛中烧制而成。采用了上述技术方案后，本专利技术使裂纹釉不单单是单色裂纹，而变成细小裂纹并伴随结晶效果，装饰手法更诱人，可作本文档来自技高网...

【技术保护点】
一种裂纹聚沫析晶釉，其特征在于它的组分和各组分质量如下：马迹泥50份～60份；方解石6份～8份；氧化锌6份～8份；碳酸锂10份～12份；高岭土3份～5份；硅酸锆10份～12份。

【技术特征摘要】
1.一种裂纹聚沫析晶釉，其特征在于它的组分和各组分质量如下：马迹泥50份～60份；方解石6份～8份；氧化锌6份～8份；碳酸锂10份～12份；高岭土3份～5份；硅酸锆10份～12份。2.根据权利要求书1所述的裂纹聚沫析晶釉，其特征在于它的组分和各组分质量...

【专利技术属性】
技术研发人员：程莉，
申请(专利权)人：程莉，
类型：发明
国别省市：湖南,43