一种光热催化剂、其制备方法和催化环己烷氧化的方法技术

本发明专利技术提供了一种催化环己烷氧化的方法，包括：环己烷在光源和光热催化剂的作用下反应，得到KA油；所述催化剂包括上述技术方案所述的催化剂。其中，催化剂包括银纳米粒子负载的单层水合三氧化钨纳米片。本发明专利技术通过上述催化剂和催化环己烷氧化的方法，本发明专利技术的催化剂合成方法简单，高效易分离，同时采用本发明专利技术的催化剂催化环己烷催化选择性高、选择性好，同时反应对设备和条件要求低。

Photothermal catalyst, preparation method and catalytic oxidation method for cyclohexane

The invention provides a method for catalytic cyclohexane oxidation, including: cyclohexane reacts under the action of light source and photothermal catalyst to obtain KA oil, and the catalyst includes the catalyst described by the above technical scheme. The catalysts include silver nanoparticles loaded monolayer hydrated tungsten trioxide nanosheets. By the method of oxidation of the catalyst and catalytic cyclohexane, the invention has the advantages of simple synthesis method, high efficiency and separation, at the same time the catalyst catalyzes the catalytic selectivity and selectivity of cyclohexane, and the reaction has low requirements on equipment and conditions at the same time.

【技术实现步骤摘要】
一种光热催化剂、其制备方法和催化环己烷氧化的方法
本专利技术涉及纳米新材料
，特别涉及一种光热催化剂、其制备方法和催化环己烷氧化的方法。
技术介绍
氧化环己烷制备环己醇和环己酮(以下简称KA油)是饱和烷烃氧化的重要反应之一，其产物环己醇、环己酮是生产尼龙-6、尼龙-66以及己二酸的主要原料，但目前工业化过程中，环己烷的总体转化率不到4％，其中KA油的选择率不到80％，KA油供求存在巨大缺口。目前报道的环己烷催化氧化反应主要通过两种途径实现，即光催化和热催化。在热催化途径中，以金属卟啉为催化剂实现了较高转化率地催化空气氧化环己烷。CN200810073804.9公开了一种超细AlOOH固载金属卟啉催化空气氧化环己烷的方法，固载催化剂催化空气氧化环己烷具有高转化率(9％以上)、高选择性(85％以上)。金属卟啉催化剂对环己烷氧化反应具有很高催化活性，但催化剂自身不稳定、活性下降得很快，难以用于工业化环己烷氧化过程。CN201110111305.6公开了一种以钛硅分子筛催化双氧水氧化环己烷的方法，获得环己烷转化率20％-70％，KA油选择性90％以上。但以双氧水为氧化剂不符合实际的工业本文档来自技高网...

【技术保护点】
一种光热催化剂，其特征在于，包括银纳米粒子和负载所述银纳米粒子的单层水合三氧化钨纳米片。

【技术特征摘要】
1.一种光热催化剂，其特征在于，包括银纳米粒子和负载所述银纳米粒子的单层水合三氧化钨纳米片。2.根据权利要求1所述的纳米片，其特征在于，所述纳米片的长度为0.1～2μm，宽度为0.1～2μm，厚度为0.5～0.7nm。3.根据权利要求1所述的纳米片，其特征在于，所述纳米片的长宽比为(1～20)∶1；所述银纳米粒子的粒径为5～15nm。4.一种光热催化剂的制备方法，其特征在于，包括：将单层水合三氧化钨纳米片分散在溶剂中，与硝酸银溶液通过真空光还原处理反应体系反应，离心，得到光热催化剂；所述真空光还原处理反应体系的光源为氙灯光源，电功率为220W，光功率为50W。5.根据权利要求4所述的制备方法，...

【专利技术属性】
技术研发人员：刘金成，麦继锦，方岩雄，
申请(专利权)人：广东工业大学，
类型：发明
国别省市：广东,44