The invention discloses a mechanical fitting strengthening process, which includes processing the mechanical parts by heat treatment carbonitriding and then processing the mechanical parts for second times. The temperature of the second mechanical machining is maintained at 540 560 degrees C, and the hardness of the mechanical fittings is enhanced. Then, the alloy powder used for the cladding treatment, when the cladding treatment, the mechanical accessories need to reach 120 140 degrees, the alloy powder is cladding, covering the surface of the mechanical parts, the thickness is 0.5 1.5mm. By adopting the mechanical parts strengthening process of the invention, the mechanical parts can achieve high strength, corrosion resistance and wear resistance.
【技术实现步骤摘要】
一种机械配件强化工艺
本专利技术涉及机械材料强化工艺，具体涉及一种机械配件强化工艺。
技术介绍
随着机械配件在各个机械系统中的广泛使用，机械配件往往为连接部件，需要承担频繁高速的往复运动，负载大，对材料的要求性能高，而机械配件的性能好坏直接影响到整个机械系统的寿命和可靠性。另一方面，由于机械系统的连接部件需要浸泡在油中，来增强机械活动的流畅性，还需要机械配件具有抗腐蚀的能力，所以如何提高机械配件的强度和硬度，抗磨损以及抗腐蚀的能力是目前需要解决的技术问题。在现有技术中在机械配件强度处理过程中需要消耗大量的能量，需要对机械配件表面进行处理时，需要重新进行表面强化处理的流程造成能源浪费和流程繁琐。
技术实现思路
本专利技术提供了一种机械配件强化工艺，用以解决现有技术中对机械配件进行强度处理以及表面强化处理时，流程繁琐，能源浪费的问题。本专利技术采用的技术方案如下：本专利技术公开了一种机械配件强化工艺，其特征在于，包括如下步骤：1)热处理碳氮共渗：将机械加工后的配件装入渗碳炉，提高渗碳炉的温度至850-870℃，并保持8-10小时；2)第二次机械加工：保持第二次机械加工的温...
【技术保护点】
一种机械配件强化工艺，其特征在于，包括如下步骤：1)热处理碳氮共渗：将机械加工后的配件装入渗碳炉，提高渗碳炉的温度至850‑870℃，并保持8‑10小时；2)第二次机械加工：保持第二次机械加工的温度为540‑560℃；3)配置合金粉末：所述合金粉末成分为镍50‑60％，铬10‑20％，铁20‑30％；4)熔覆处理：首先将机械配件表面经超声波清洗去污，并采用含氟气体去除钝化膜，然后让机械配件的温度达到120‑140℃，随后将合金粉末进行熔覆处理，覆在所述机械配件表面，厚度为0.5‑1.5mm，并在100‑150℃的保温炉中下烘烤1小时。
【技术特征摘要】
1.一种机械配件强化工艺，其特征在于，包括如下步骤：1)热处理碳氮共渗：将机械加工后的配件装入渗碳炉，提高渗碳炉的温度至850-870℃，并保持8-10小时；2)第二次机械加工：保持第二次机械加工的温度为540-560℃；3)配置合金粉末：所述合金粉末成分为镍50-60％，铬10-20％，铁20-30％；4)熔覆处理：首先将机械配件表面经超声波清洗去污，并采用含氟气体去除钝化膜，然后让机械配件的温度达到120-140℃，随后将合金粉末进行熔覆处理，覆在所述机械配件表面，厚度为0.5-1.5mm，并在100-150℃的保温炉中下烘烤1小时。2.根据权利要求1所述的机械配件强化工艺，其特征在于，在所述第二次机械加工之后需要对所述机械配件进行热处理淬火，将加工后的机械配件迅速放...