The invention discloses a cement stabilizer, which is characterized in that 60 parts of clinker, 50 parts of mixed material, 7 phr of fluorogypsum, 1 phr of polyvinyl formal, one carrier, plasticizer, rust inhibitor, one or two kinds of sodium nitrite and sodium thiosulfate, or two kinds of 0.5 parts, including slag, coal gangue and fly ash. For the further improvement of the invention, the weight ratio of the carrier, plasticizer and rust inhibitor ingredient is 26:15:6. The invention has the beneficial effect: the energy saving cement with shortened solidification time of the invention has good sticky viscosity and is more durable after solidification.
【技术实现步骤摘要】
一种水泥安定剂
本专利技术涉及水泥
，尤其涉及一种水泥安定剂。
技术介绍
目前水泥是一种应用范围广泛的建筑材料，施工时需要和一定比例的沙石配合使用，一般现场对所加的沙石粒度大小要求不严格，实际上沙石粒度大小对水泥的性能影响很大，如果沙石粒度大，界面粘合力增强，水泥强度提高，但是与其配合的水泥用量相应多了，增加了成本；如果沙石粒度小，则比表面积大，可使水泥用水量增加，塑性收缩增大，施工早期开裂的可能性提高。再有水泥灌浆后需一段时间才能凝固。不能满足一些需要快速凝固特殊场合下使用。
技术实现思路
鉴于此，本专利技术提供了一种水泥安定剂，其特征在于，包括熟料60份、混合材料50份、氟石膏7份、聚乙烯醇缩甲醛1份，载体、增塑剂、阻锈剂，亚硝酸钠与硫代硫酸钠中的一种或二种0.5份，所述的混合材料包括矿渣、煤矸石、粉煤灰。对本专利技术的进一步改进，所述载体、增塑剂、阻锈剂成分重量比例为26：15：6。采用上述技术方案，具有如下有益效果：本专利技术的有益效果：本专利技术的缩短凝固时间的节能水泥黏粘性良好，凝固后更加坚固耐用。具体实施方式一种水泥安定剂，其特征在于，包括熟料60份、混合材料50份、氟石膏7份、聚乙烯醇缩甲醛1份，载体、增塑剂、阻锈剂，亚硝酸钠与硫代硫酸钠中的一种或二种0.5份，所述的混合材料包括矿渣、煤矸石、粉煤灰。对本专利技术的进一步改进，所述载体、增塑剂、阻锈剂成分重量比例为26：15：6。采用上述技术方案，具有如下有益效果：本专利技术的有益效果：本专利技术的缩短凝固时间的节能水泥黏粘性良好，凝固后更加坚固耐用。以上描述了本专利技术的基本原理和主要特...
【技术保护点】
一种水泥安定剂，其特征在于，包括熟料60份、混合材料50份、氟石膏7份、聚乙烯醇缩甲醛1份，载体、增塑剂、阻锈剂，亚硝酸钠与硫代硫酸钠中的一种或二种0.5份，所述的混合材料包括矿渣、煤矸石、粉煤灰。
【技术特征摘要】
1.一种水泥安定剂，其特征在于，包括熟料60份、混合材料50份、氟石膏7份、聚乙烯醇缩甲醛1份，载体、增塑剂、阻锈剂，亚硝酸钠与硫代硫酸钠中的一种或二种0...
【专利技术属性】
技术研发人员：李善福，
申请(专利权)人：徐州市龙山水泥有限公司，
类型：发明
国别省市：江苏,32